Observation of the early stages of environmental contamination in graphene by friction force.

Exposure to ambient air contaminates the surface of graphene sheets. Contamination may arise from different sources, and its nature alters the frictional behavior of the material. These changes in friction enable the observation of the early stages of contaminants' adsorption in graphene.

Thickness measurements of graphene oxide flakes using atomic force microscopy: results of an international interlaboratory comparison.

Flake thickness is one of the defining properties of graphene-related 2D materials (GR2Ms), and therefore requires reliable, accurate, and reproducible measurements with well-understood uncertainties. This is needed regardless of the production method or manufacturer because it is important for all GR2M products to be globally comparable. An international interlaboratory comparison on thickness measurements of graphene oxide flakes using atomic force microscopy has been completed in technical working area 41 of versailles project on advanced materials and standards.

Giant and Tunable Anisotropy of Nanoscale Friction in Graphene.

The nanoscale friction between an atomic force microscopy tip and graphene is investigated using friction force microscopy (FFM). During the tip movement, friction forces are observed to increase and then saturate in a highly anisotropic manner. As a result, the friction forces in graphene are highly dependent on the scanning direction: under some conditions, the energy dissipated along the armchair direction can be 80% higher than along the zigzag direction.

Raman signature of graphene superlattices.

When two identical two-dimensional periodic structures are superposed, a mismatch rotation angle between the structures generates a superlattice. This effect is commonly observed in graphite, where the rotation between graphene layers generates Moiré patterns in scanning tunneling microscopy images. Here, a study of intravalley and intervalley double-resonance Raman processes mediated by static potentials in rotationally stacked bilayer graphene is presented.