Synthesis and characterization of the crystal structure, the magnetic and the electrochemical properties of the new fluorophosphate LiNaFe[PO4]F.

The new compound LiNaFe[PO(4)]F was synthesized by a solid state reaction route, and its crystal structure was determined using neutron powder diffraction data. LiNaFe[PO(4)]F was characterized by (57)Fe Mössbauer spectroscopy, magnetic susceptibility, specific heat capacity, and electrochemical measurements. LiNaFe[PO(4)]F crystallizes with orthorhombic symmetry, space group Pnma, with a = 10.

Antifluorite-type lithium chromium oxide nitrides: synthesis, structure, order, and electrochemical properties.

Antifluorite-type lithium chromium oxide nitrides were prepared by solid-state reaction of Li(3)N, Li(2)O, and Cr(2)N. Depending on the reaction time and starting Li/Cr and O/Cr ratios, either an ordered or a disordered phase (or mixtures of both) is obtained. The formation of the former is favored by short reaction times and low Cr/O ratios whereas the formation of the latter is favored by higher Cr/O ratios and longer reaction times.