8.6% Efficient CZTSSe Solar Cells Sprayed from Water-Ethanol CZTS Colloidal Solutions.

Copper zinc tin sulfide-selenide, Cu2ZnSn(S1-xSex)4 (CZTSSe), thin film photovoltaic devices were fabricated using a fast and environmentally friendly preparation method, consisting of the following steps: An instantaneous synthesis of a Cu-Zn-Sn-S (no Se) colloid, a nonpyrolytic spray of a dispersion of this colloid in a water-ethanol mixture, and a sequential annealing first in a N2 atmosphere and second in a Se atmosphere. The achievement of cell efficiencies up to 8.6% under AM1.

Sensitization of nanocrystalline TiO2 with black absorbers based on Os and Ru polypyridine complexes.

New metal complexes of the type [M(H3tcterpy)LY]+ (where M = Os(II) or Ru(II), L = substituted or unsubstituted bipyridine or pyridylquinoline, and Y = Cl-, I-, or SCN-) have been designed, synthesized, and characterized in view of their application for dye-sensitized solar cells (DSSCs). The Os dyes show a very broad absorption, and correspondingly, the DSSCs show an unprecedented spectral response in the NIR, with an onset at 1100 nm, reaching values of about 50% at 900 nm. The integrated photocurrent of some of such Os dyes is similar to that of the well-known [Ru(Htcterpy)(NCS)3](TBA) and superior to that of the [Ru(Hdcbpy)2(NCS)2](TBA)2 sensitizer.