Evidence of polyamorphic transitions during densified SiO glass annealing.

In situ X-ray scattering monitoring is carried out during temperature annealing on different densified SiO glasses. Density fluctuations and intermediate range coherence from X-ray scattering (small-angle X-ray scattering) and diffraction (wide angle X-ray scattering) evidence a maximum in their evolution at the same relaxation time. These extrema confirm the existence of an intermediate transitory disordered state between the two more ordered high and low density amorphous states.

Relaxation study of pre-densified silica glasses under 2.5 MeV electron irradiation.

We examined the "relaxation properties" of pre-densified synthetic fused silica glass under 2.5 MeV electron irradiation. The densification of the glass was either obtained by hot compression (5 GPa-350 °C and 5 GPa-1000 °C) or via a thermal treatment increasing its fictive temperature (T = 1050, 1250 and 1400 °C).

A-thermal elastic behavior of silicate glasses.

Depending on the composition of silicate glasses, their elastic moduli can increase or decrease as function of the temperature. Studying the Brillouin frequency shift of these glasses versus temperature allows the a-thermal composition corresponding to an intermediate glass to be determined. In an intermediate glass, the elastic moduli are independent of the temperature over a large temperature range.