A self-encapsulated porous Sb-C nanocomposite anode with excellent Na-ion storage performance.

In this study, a self-encapsulated Sb-C nanocomposite as an anode material for sodium-ion batteries (SIBs) was successfully synthesised using an SbCl-citrate complex precursor, followed by a drying and calcination process under an inert N atmosphere. When the molar ratio of SbCl to citric acid was varied from 1 : 1 to 1 : 4, the Sb-C nanocomposite with a molar ratio of 1 : 3 (Sb-C3) exhibited the highest specific surface area (265.97 m g) and pore volume (0.

Facile Synthesis of Si@SiC Composite as an Anode Material for Lithium-Ion Batteries.

Here, we propose a simple method for direct synthesis of a Si@SiC composite derived from a SiO@C precursor via a Mg thermal reduction method as an anode material for Li-ion batteries. Owing to the extremely high exothermic reaction between SiO and Mg, along with the presence of carbon, SiC can be spontaneously produced with the formation of Si. The synthesized Si@SiC was composed of well-mixed SiC and Si nanocrystallites.

Composite Gel Polymer Electrolyte Based on Poly(vinylidene fluoride-hexafluoropropylene) (PVDF-HFP) with Modified Aluminum-Doped Lithium Lanthanum Titanate (A-LLTO) for High-Performance Lithium Rechargeable Batteries.

A composite gel polymer electrolyte (CGPE) based on poly(vinylidene fluoride-hexafluoropropylene) (PVDF-HFP) polymer that includes Al-doped Li0.33La0.56TiO3 (A-LLTO) particles covered with a modified SiO2 (m-SiO2) layer was fabricated through a simple solution-casting method followed by activation in a liquid electrolyte.

Conducting additive-free amorphous GeO2/C composite as a high capacity and long-term stability anode for lithium ion batteries.

In this study, a novel method has been proposed for synthesizing amorphous GeO2/C composites. The amorphous GeO2/C composite without carbon black as an electrode for Li-ion batteries exhibited a high specific capacity of 914 mA h g(-1) at the rate of C/2 and enhanced rate capability. The amorphous GeO2/C electrode exhibited excellent electrochemical stability with a 95.

Facile and cost effective synthesis of mesoporous spinel NiCo2O4 as an anode for high lithium storage capacity.

To fulfill the high power and high energy density demands for Li-ion batteries (LIBs) new anode materials need to be explored to replace conventional graphite. Herein, we report the urea assisted facile co-precipitation synthesis of spinel NiCo2O4 and its application as an anode material for LIBs. The synthesized NiCo2O4 exhibited an urchin-like microstructure and polycrystalline and mesoporous nature.