Melamine-formaldehyde derived porous carbons for adsorption of CO capture.

In this work, we report carbon adsorbents obtained from high nitrogen content melamine-formaldehyde resin as starting material and mesoporous zeolite MCM-41 as template through nanocasting technique. To synthesize different carbon structure adsorbents with improved textural and surface properties, the material undergo carbonization followed by physical activation under CO atmosphere at different temperatures. Characterizations of the adsorbents using SEM, TEM, XPS, nitrogen sorption, CHN, TKN, and TPD have been carried out.

Development of nitrogen enriched nanostructured carbon adsorbents for CO2 capture.

Nanostructured carbon adsorbents containing high nitrogen content were developed by templating melamine-formaldehyde resin in the pores of mesoporous silica by nanocasting technique. A series of adsorbents were prepared by altering the carbonization temperature from 400 to 700 °C and characterized in terms of their textural and morphological properties. CO2 adsorption performance was investigated at various temperatures from 30 to 100 °C by using a thermogravimetric analyzer under varying CO2 concentrations.

Mesoporous carbon adsorbents from melamine-formaldehyde resin using nanocasting technique for CO2 adsorption.

Mesoporous carbon adsorbents, having high nitrogen content, were synthesized via nanocasting technique with melamine-formaldehyde resin as precursor and mesoporous silica as template. A series of adsorbents were prepared by varying the carbonization temperature from 400 to 700°C. Adsorbents were characterized thoroughly by nitrogen sorption, X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM), thermogravimetric analysis (TGA), elemental (CHN) analysis, Fourier transform infrared (FTIR) spectroscopy and Boehm titration.