Enhancing the Photovoltaic Performance of Perovskite Solar Cells with a Down-Conversion Eu-Complex.

Organometal halide perovskite solar cells (PSCs) have shown high photovoltaic performance but poor utilization of ultraviolet (UV) irradiation. Lanthanide complexes have a wide absorption range in the UV region and they can down-convert the absorbed UV light into visible light, which provides a possibility for PSCs to utilize UV light for higher photocurrent, efficiency, and stability. In this study, we use a transparent luminescent down-converting layer (LDL) of Eu-4,7-diphenyl-1,10-phenanthroline (Eu-complex) to improve the light utilization efficiency of PSCs.

TiO2 Sub-microsphere Film as Scaffold Layer for Efficient Perovskite Solar Cells.

TiO2 sub-microspheres composed of anatase granular-like nanocrystallines with an average diameter ∼250 nm are synthesized using sol-gel method and employed as the scaffold layer for efficient mesocopic perovskite solar cells. Compared with mesoporous TiO2 films composed of ∼18 nm nanoparticles, the sub-microsphere films show superior light-trapping characteristics and significantly improve the light-harvesting capability of the solar cells. In addition, the charge-transport performance is also dramatically improved according to the transient photocurrent decay despite there being no significant difference in the perovskite layer surface morphology.

Low molecular mass organogelator based gel electrolyte with effective charge transport property for long-term stable quasi-solid-state dye-sensitized solar cells.

Stable quasi-solid-state dye-sensitized solar cells (DSC) were fabricated using 12-hydroxystearic acid as a low molecular mass organogelator (LMOG) to form gel electrolyte. TEM image of the gel exhibited the self-assembled network constructed by the LMOG, which hindered flow and volatilization of the liquid. The formation of less-mobile polyiodide ions such as I 3 (-) and I 5 (-) confirmed by Raman spectroscopy increased the conductivity of the gel electrolytes by electronic conduction process, which should be rationalized by the Grotthuss-type electron exchange mechanism caused by rather packed polyiodide species in the electrolytes.