The Microstructure and Thermal Conductive Behavior of Three-Dimensional Carbon/Carbon Composites with Ultrahigh Thermal Conductivity.

Carbon-based composite materials, denoted as C/C composites and possessing high thermal conductivity, were synthesized utilizing a three-dimensional (3D) preform methodology. This involved the orthogonal weaving of mesophase pitch-based fibers in an X (Y) direction derived from low-temperature carbonization, and commercial PAN-based carbon fibers in a Z direction. The 3D preforms were saturated with mesophase pitch in their raw state through a hot-pressing process, which was executed under relatively low pressure at a predetermined temperature.

Preparation, Microstructure and Thermal Properties of Aligned Mesophase Pitch-Based Carbon Fiber Interface Materials by an Electrostatic Flocking Method.

The mesophase pitch-based carbon fiber interface material (TIM) with a vertical array was prepared by using mesophase pitch-based short-cut fibers (MPCFs) and 3016 epoxy resin as raw materials and carbon nanotubes (CNTs) as additives through electrostatic flocking and resin pouring molding process. The microstructure and thermal properties of the interface were analyzed by using a scanning electron microscope (SEM), laser thermal conductivity and thermal infrared imaging methods. The results indicate that the plate spacing and fusing voltage have a significant impact on the orientation of the arrays formed by mesophase pitch-based carbon fibers.