Experimental Study of the Moisture Resistance of Cement Mortar Using Pozzolan Materials and Calcium Stearate.

Nanosilica and diatomite are pozzolanic resources rich in SiO. In this study, the purpose of this study was to improve the moisture resistance of the specimen by producing a mixed material using pozzolanic materials and calcium stearate and adding it to cement mortar while stirring. The results showed that the hydration reaction was not activated when calcium stearate adhered to the fine particles of nanosilica; it existed simply in the form of a filler inside the specimen.

Properties and Durability of Cement Mortar Using Calcium Stearate and Natural Pozzolan for Concrete Surface Treatment.

Applying a concrete surface treatment method (epoxy or primer) can prevent water from penetrating concrete through surface pores. However, if the concrete surface is damaged, the subsequent reconstruction can be expensive and time-consuming. Concrete that is resistant to internal and external water has been extensively developed and used to supplement the surface treatment method.

Experimental Study on the Evaluation of Physical Performance and Durability of Cement Mortar Mixed with Water Repellent Impregnated Natural Zeolite.

To complement the shortcomings of concrete surface treatment technology and improve the durability of concrete structure, the purpose of this study was to impregnate water-repellent performance into natural zeolite, which has many pores inside, to achieve water-repellent performance inside concrete. The physical performance and durability of cement mortar mixed with water-repellent natural zeolite was evaluated. Cement mortars were prepared by mixing ZWR1%, 3%, and 5% (ZWR: Zeolite + Water Repellent impregnation) in cement powder, and compressive strength, contact angle, water penetration test, resistance chloride penetration test, chloride diffusion coefficient, and accelerated carbonation test were evaluated.