Stress-transfer from polymer substrates to monolayer and few-layer graphenes.

In the present study, the stress transfer mechanism in graphene-polymer systems under tension is examined experimentally using the technique of laser Raman microscopy. We discuss in detail the effect of graphene edge geometry, lateral size and thickness which need to be taken under consideration when using graphene as a protective layer. The systems examined were composed of graphene flakes with a large length (over ∼50 microns) and a thickness of one to three layers simply deposited onto PMMA substrates which were then loaded to a tension of ∼1.

Wrinkling formation in simply-supported graphenes under tension and compression loadings.

Wrinkles in supported graphenes can be formed either by uniaxial compression or uniaxial tension beyond a certain critical load depending on the mode of loading. In the first case, the wrinkling direction is normal to the compression axis whereas in tension, wrinkles of the same pattern are formed parallel to the loading direction due to Poisson's (lateral) contraction. Herein we show by direct AFM observations that in simply-supported graphenes such instabilities appear as periodic wrinkles over existing stochastic undulations caused by the underlying-substrate-roughness.