Bitumen-Based Poroelastic Pavements: Successful Improvements and Remaining Issues.

This article presents the development process of designing and testing poroelastic pavement based on highly polymer-modified bitumen. Poroelastic wearing course was composed of mineral and rubber aggregate mixed with highly polymer-modified bitumen, in contrast to previous trials, during which polyurethane resins were mainly used as binder, which led to several serious technological problems concerning difficult production, insufficient bonding to the base layer, and unsatisfactory durability. The laboratory testing phase was aimed at finding the proper composition of the poroelastic mixture that would ensure required internal shear strength and proper bonding of the poroelastic layer with the base layer.

Fatigue Performance of Double-Layered Asphalt Concrete Beams Reinforced with New Type of Geocomposites.

The reinforcement of asphalt layers with geosynthetics has been used for several decades, but proper evaluation of the influence of these materials on pavement fatigue life is still a challenging task. The presented study investigates a novel approach to the reinforcement of asphalt layers using a new type of geogrid composite, in which square or hexagonal polypropylene stiff monolithic paving grid with integral junctions is bonded to polypropylene non-woven paving fabric. The laboratory fatigue tests were performed on large asphalt concrete beams reinforced with the new type of geocomposite.

Initial Field Validation of Poroelastic Pavement Made with Crumb Rubber, Mineral Aggregate and Highly Polymer-Modified Bitumen.

Tire/road noise in most driving conditions dominates other sources of traffic noise. One of the most efficient ways of reducing tire/road noise is to use the so-called "low noise pavement". According to numerous studies, at present, poroelastic road pavement that is composed of rubber and mineral aggregate and polyurethane or bituminous binder gives the best noise reduction up to 12 dB.

Influence of Selected Warm Mix Asphalt Additives on Cracking Susceptibility of Asphalt Mixtures.

Warm mix asphalt (WMA) has been widely accepted as a future asphalt paving technology. Besides clear advantages, there are still some concerns regarding durability and long-term performance of pavements made with this type of asphalt mixtures. One of the most important issues is low temperature behaviour of WMA because certain additives used for temperature reduction can affect bitumen properties.

Influence of Bitumen Type and Asphalt Mixture Composition on Low-Temperature Strength Properties According to Various Test Methods.

temperatures, action transverse cracks can appear in asphalt pavements as a result of thermal stresses that exceed the fracture strength of materials used in asphalt layers. To better understand thermal cracking phenomenon, strength properties of different asphalt mixtures were investigated. Four test methods were used to assess the influence of bitumen type and mixture composition on tensile strength properties of asphalt mixtures: tensile strength was measured using the thermal stress restrained specimen test (TSRST) and the uniaxial tension stress test (UTST), flexural strength was measured using the bending beam test (BBT), and fracture toughness was measured using the semi-circular bending test (SCB).

Evaluation of Asphalt Mixture Low-Temperature Performance in Bending Beam Creep Test.

Low-temperature cracking is one of the most common road pavement distress types in Poland. While bitumen performance can be evaluated in detail using bending beam rheometer (BBR) or dynamic shear rheometer (DSR) tests, none of the normalized test methods gives a comprehensive representation of low-temperature performance of the asphalt mixtures. This article presents the Bending Beam Creep test performed at temperatures from -20 °C to +10 °C in order to evaluate the low-temperature performance of asphalt mixtures.