The effect of phytosphingosine associated with tooth brushing on color change, surface roughness, and microhardness of dental enamel - an in vitro and in situ study.

Objective: This study evaluated the in vitro and in situ effects of phytosphingosine (PHS) associated with tooth brushing on color stability, surface roughness, and microhardness of dental enamel.

Methods: Sixty-four specimens of bovine teeth (6 × 6 × 2 mm) were separated into 8 groups (n = 8): S + TB: PHS (spray) + tooth brushing; TB + S: tooth brushing + PHS (spray); I + TB: PHS (immersion) + tooth brushing; TB + I: tooth brushing + PHS (immersion); TB: tooth brushing; S: PHS spray; I: immersion in PHS solution, and Saliva: immersion in saliva. Tooth brushing simulation (Mavtec, Brazil) was performed (356 rpm on 3.

Using denture cleansers to control biofilm from dentures and brushes: A randomized crossover clinical trial.

Purpose: To evaluate the effects of 0.2% sodium hypochlorite, Efferdent (Prestige Consumer Healthcare), and 6.25% Ricinus communis on biofilm removal and antimicrobial action on dentures and brushes using nonimmersion or immersion protocols for the brushes.

Effect of phytosphingosine on staining resistance and microhardness of tooth enamel.

Objective: To evaluate the protective effect of phytosphingosine (PHS) against staining on dental enamel.

Materials And Methods: Ninety-six specimens of bovine teeth (6 mm × 6 mm × 2 mm) were cut, and initial color (Easyshade, VITA), microhardness (HMV-2, Shimadzu) and fluorescence (Matlabs software, Matworks) measurements were performed. Specimens were separated into four groups according to the treatments: Distilled water (control); Human saliva (HS); PHS; PHS + HS.

In Vitro Analysis of Surface Roughness of Acrylic Resin Exposed to the Combined Hygiene Method of Brushing and Immersion in Ricinus communis and Sodium Hypochlorite.

Purpose: To evaluate a solution based on Ricinus communis (Castor oil) for denture cleansing, comparing it to sodium hypochlorite (NaOCl) for the surface roughness of heat-polymerized acrylic resin.

Materials And Methods: Forty polished and unpolished resin specimens (90 × 30 × 4 mm) were evaluated before and after their exposure to protocol hygiene: brushing the specimens with a specific denture brush and mild soap for 3 minutes, three times a day, and immersing them in hygiene solutions (0.25% NaOCl-S1 and 0.

Effects of Denture Cleansers on Heat-Polymerized Acrylic Resin: A Five-Year-Simulated Period of Use.

This study evaluated color stability, surface roughness and flexural strength of acrylic resin after immersion in alkaline peroxide and alkaline hypochlorite solutions, simulating a five-year-period of use. Sixty disc-shaped (16 x 4 mm) and 60 rectangular specimens (65 x 10 x 3.3 mm) were prepared from heat-polymerized acrylic resin (Lucitone 550) and assigned to 3 groups (n = 20) of immersion (20 min): C1: distilled water; AP: warm water and one alkaline peroxide tablet; SH: 0.

Adverse effects on PMMA caused by mechanical and combined methods of denture cleansing.

This study evaluated the abrasiveness of mechanical and combined methods of denture hygiene, by the analysis of mass loss and surface roughness. Acrylic resin specimens (Plexiglass) were brushed by a tooth brushing machine (Mavtec) with a soft brush (Tek) and water (control) or four dentifrices (Sorriso, Colgate, Polident and Corega) (Experimental groups) for 50 min, representing one year of brushing (mechanical method). After brushing, the specimens were immersed in 0.