Nb-Based Catalysts for the Valorization of Furfural into Valuable Product through in One-Pot Reaction.

Nb-based catalysts supported on porous silica with different textural properties have been synthesized, characterized, and tested in the one-pot reaction of furfural to obtain valuable chemicals. The catalytic results reveal that the presence of fluoride in the synthesis, which limits the growing of the porous silica, limits diffusional problems of the porous silica, obtaining higher conversion values at shorter reaction times. On the other hand, the incorporation of NbO species in the porous silica provides Lewis acid sites and a small proportion of Brönsted acid sites, in such a way that the main products are alkyl furfuryl ethers, which can be used as fuel additives.

Modification of the Textural Properties of Chitosan to Obtain Biochars for CO-Capture Processes.

Three chitosans with different morphologies have been used (commercial chitosan powder, chitosan in film form and chitosan in globular form synthesized by the freeze-dried method) for the synthesis of biochars. The pyrolytic treatment has revealed that the biochar synthesized from the chitosan formed by the freeze-dried method reaches the highest CO-adsorption capacity (4.11 mmol/g at 0 °C and a pressure of 1 bar) due to this adsorbent is highly microporous.

Influence of Structure-modifying Agents in the Synthesis of Zr-doped SBA-15 Silica and Their Use as Catalysts in the Furfural Hydrogenation to Obtain High Value-added Products through the Meerwein-Ponndorf-Verley Reduction.

Zr-doped mesoporous silicas with different textural parameters have been synthesized in the presence of structure-modifying agents, and then characterized by X-ray diffraction (XRD), transmission electron microscopy (TEM), N₂ adsorption-desorption at -196 °C, NH₃ thermoprogrammed desorption (NH₃⁻TPD), CO₂ thermoprogrammed desorption (CO₂⁻TPD), and X-ray photoelectron spectroscopy (XPS). These porous materials were evaluated in the furfural hydrogenation through the Meerwein-Ponndorf-Verley (MPV) reaction. The catalytic results indicate that the catalyst synthesized under hydrothermal conditions and adding a pore expander agent is more active and selective to furfuryl alcohol.

Porous Silicon-Based Catalysts for the Dehydration of Glycerol to High Value-Added Products.

Increasing worldwide biodiesel production has led to the generation of an important glycerol surplus, which needs to be valorized in order to improve the economic and environmental sustainability of the biodiesel industry. In this context, glycerol dehydration to acrolein by acid catalysis appears to be a potential route of glycerol valorization, since acrolein is an important intermediate for many chemical industries. The main drawback of this catalytic process is catalyst deactivation.

Selective Production of 2-Methylfuran by Gas-Phase Hydrogenation of Furfural on Copper Incorporated by Complexation in Mesoporous Silica Catalysts.

Copper species have been incorporated in mesoporous silica (MS) through complexation with the amine groups of dodecylamine, which was used as a structure-directing agent in the synthesis. A series of Cu/SiO catalysts (xCu-MS) with copper loadings (x) from 2.5 to 20 wt % was synthesized and evaluated in the gas-phase hydrogenation of furfural (FUR).