Microstructural and Electrochemical Study: Pitting Corrosion Mechanism on A390 Al-Si Alloy and Ce-Mo Treatment as a Better Corrosion Protection.

Sulfuric acid anodizing assisted by a hydrothermal sealing with inhibitors [Ce-Mo] was used to prevent pitting corrosion on spray-deposited hypereutectic Al-Si alloy (A390). An investigation concerning the evaluation of pitting corrosion resistance on the anodic oxide thin film with ions incorporated was carried out in NaCl solution using electrochemical measurements (i.e.

Physical, mechanical properties and antimicrobial analysis of a novel CaO·AlO compound reinforced with Al or Ag particles.

Ceramic-metal (CaO·AlO-Al and CaO·AlO-Ag) compounds were prepared by mechanical milling and consolidated through an in-situ sintering process. The aim of this work is to study the effects of the Al and Ag particles to ceramic-base compound, primarily in the microstructure, and its mechanical and antimicrobial properties. Chemical systems with a 1:1 M ratio between CaCO and AlO powder were formed, with the addition of 10 wt% Al or 10 wt% Ag, respectively.

A piezoelectric plethysmograph sensor based on a Pt wire implanted lead lanthanum zirconate titanate bulk ceramic.

This work reports on the development of a Lead Lanthanum Zirconate Titanate (PLZT) bulk ferroelectric poled ceramic structure as a Piezoelectric Plethysmograph (PZPG) sensor. The ceramic was implanted during its fabrication with a platinum (Pt) wire which works as an internal electrode. The ceramic was then submitted to an experimental setup in order to validate and determine the Pt-wire mechanical effects.