Removable partial dentures: use of rapid prototyping.

The CAD/CAM technology associated with rapid prototyping (RP) is already widely used in the fabrication of all-ceramic fixed prostheses and in the biomedical area; however, the use of this technology for the manufacture of metal frames for removable dentures is new. This work reports the results of a literature review conducted on the use of CAD/CAM and RP in the manufacture of removable partial dentures.

Effect of brushing with conventional versus whitening dentifrices on surface roughness and biofilm formation of dental ceramics.

The aim of this study was to evaluate the effect of conventional and whitening dentifrices on the weight loss, surface roughness, and early in situ biofilm formation on the surface of dental ceramics. Standardized feldspar ceramic specimens (Vita VM7 and Vita VM13) were submitted to the following experimental conditions: no brushing; brushing without a dentifrice; brushing with a conventional dentifrice; and brushing with a whitening dentifrice. A brushing machine was used to simulate brushing.

Marginal and internal discrepancies related to margin design of ceramic crowns fabricated by a CAD/CAM system.

Purpose: The aim of this study was to evaluate the marginal discrepancy (MD) and internal discrepancy (ID) of ceramic crowns manufactured by a CAD/CAM system, having different finish lines. The hypotheses tested were that the finish line type would not influence the MD or ID of the crowns, and ID would not change in different regions.

Materials And Methods: Three aluminum master dies (height: 5.

Effect of different polymerization devices on the degree of conversion and the physical properties of an indirect resin composite.

Polymerization of indirect resin composites (IRC) is carried out in the 'laboratories using special photo-polymerization devices to achieve a higher degree of conversion (DC). Such devices present variation in chambers and light output which may have consequences on the chemical and physical properties of IRCs. This study evaluated the effect of different polymerization devices on the flexural strength, Vickers microhardness and DC of an IRC.

Conversion degree of indirect resin composites and effect of thermocycling on their physical properties.

Purpose: This study evaluated the degree of conversion (DC) of four indirect resin composites (IRCs) with various compositions processed in different polymerization units and investigated the effect of thermal aging on the flexural strength and Vicker's microhardness.

Materials And Methods: Specimens were prepared from four IRC materials, namely Gr 1: Resilab (Wilcos); Gr2: Sinfony (3M ESPE); Gr3: VITA VMLC (VITA Zahnfabrik); Gr4: VITA Zeta (VITA Zahnfabrik) using special molds for flexural strength test (N = 80, n = 10 per group) (25 x 2 x 2 mm(3), ISO 4049), for Vicker's microhardness test (N = 80, n = 10 per group) (5 x 4 mm(2)) and for DC (N = 10) using FT-Raman Spectroscopy. For both flexural strength and microhardness tests, half of the specimens were randomly stored in distilled water at 37 degrees C for 24 hours (Groups 1 to 4), and the other half (Groups 5 to 8) were subjected to thermocycling (5000 cycles, 5 to 55 +/- 1 degree C, dwell time: 30 seconds).

Adhesive cementation of zirconia posts to root dentin: evaluation of the mechanical cycling effect.

This study evaluated the effect of mechanical cycling on the bond strength of zirconia posts to root dentin. Thirty single-rooted human teeth were transversally sectioned to a length of 16 mm. The canal preparation was performed with zirconia post system drills (CosmoPost, Ivoclar) to a depth of 12 mm.

Shear bond strength between metal alloy and a ceramic system, submitted to different thermocycling immersion times.

The aim of this study was to evaluate the shear bond strength of Co-Cr and Ni-Cr metal alloys and a specific ceramic, submitted to different thermocycling immersion times. Sixty metal-ceramic specimens were confectioned and standardized in cylindricalformat. Three thermocycling conditions were evaluated: without thermocycling, 3,000 cycles (5 degrees C/55 degrees C+/-1) with 30s of immersion time and 3,000 cycles (5 degrees C/55 degrees C+/-1) with 60s.

Effect of adhesive system type and tooth region on the bond strength to dentin.

Purpose: This study evaluated the bond strength of two etch-and-rinse adhesive systems (two- and three-step) and a self-etching system to coronal and root canal dentin.

Materials And Methods: The root canals of 30 human incisors and canines were instrumented and prepared with burs. The posts used for luting were duplicated with dual resin cement (Duo-link) inside Aestheti Plus #2 molds.