Anodes for Li-ion batteries prepared from microcrystalline silicon and enabled by binder's chemistry and pseudo-self-healing.

Silicon, while suffering from major degradation issues, has been recognized as a next promising material to replace currently used graphite in the anodes of Li-ion batteries. Several pathways to mitigate the capacity fading of silicon has been proposed, including optimization of the electrode composition. Within the present work we evaluated different binder formulations to improve the long-term performance of the Li-ion batteries' anodes based on industrial grade silicon (Si) which is typically characterized by a particle sizes ranging from 100 nm to 5.

Silicon-Carbon composite anodes from industrial battery grade silicon.

In this work, silicon/carbon composites for anode electrodes of Li-ion batteries are prepared from Elkem's Silgrain® line. Gentle ball milling is used to reduce particle size of Silgrain, and the resulting Si powder consists of micrometic Si with some impurities. Silicon/carbon composite with CMC/SBR as a dual binder can achieve more than 1200 cycles with a capacity of 1000 mAh g of Si.