Mechanical properties of dual-polymerizing resin-core material, dual-polymerizing resin cement, and bulk-fill composite resin used for restoring endodontically treated teeth.

Statement Of Problem: How resin-based material and a light-activation protocol influence the mechanical properties of materials used to cement glass fiber post-and-cores in endodontically treated teeth is unclear.

Purpose: The purpose of this in vitro study was to evaluate the influence of immediate or 5-minute delayed light activation on the mechanical properties of dual-polymerizing resin cements and dual-polymerizing resin-core materials compared with bulk-fill composite resins.

Material And Methods: Nine resin-based materials were tested: 4 dual-polymerizing resin-core materials, (Allcem Core; FGM, LuxaCore Z; DMG, Rebilda DC; VOCO, and (Clearfil DC Core Plus; KURARAY), 3 dual-polymerizing resin cements, (RelyX Universal; 3M ESPE, RelyX U200; 3M ESPE, and Allcem Dual; FGM), and 2 bulk-fill composite resins, (Opus Bulk Fill APS; FGM, and Filtek One Bulk Fill; 3M ESPE).

Survival of severely compromised endodontically treated teeth restored with or without a fiber glass post.

Objective: The use of a fiber glass post (FGP) type and choice of FGP diameter to restore endodontically treated incisors without ferrule is controversial. This study evaluated survival rate and failure mode of severely compromised central incisors without ferrule rehabilitated using resin-based composite (RBC) with or without FGP with different diameters.

Methodology: A total of 60 decoronated bovine incisors without a ferrule were endodontically treated and prepared for 1.

Effect of surface treatment of ethylene vinyl acetate on the delamination of custom-fitted mouthguards.

Background/aim: Contamination of ethylene vinyl acetate (EVA) during mouthguard fabrication can cause delamination. The study evaluated the effects of different EVA surface treatments on the contact angle, laminate bond strength, and elongation capacity.

Materials And Methods: Specimens of two bonded EVA plates were prepared (n = 30).