Fabrication of nanoporous TiO2 hollow capsules using core-shell silica nanoparticle templates.

We report on the fabrication of the nanoporous TiO2 hollow capsules using core-shell silica nanoparticle templates. The thickness of the capsules can be simply controlled by varying the amount of the TiO2 precursor. The resulting nanoporous capsules exhibited the high specific surface area and the large pore volume of 103-180 m2/g and 0.

Superconducting junction of a single-crystalline au nanowire for an ideal Josephson device.

We report on the fabrication and measurements of a superconducting junction of a single-crystalline Au nanowire, connected to Al electrodes. The current-voltage characteristic curve shows a clear supercurrent branch below the superconducting transition temperature of Al and quantized voltage plateaus on application of microwave radiation, as expected from Josephson relations. Highly transparent (0.

Electric property evolution of structurally defected multilayer graphene.

We report on the influence of structural disorder on the electrical properties of multilayer graphene (MLG). Exponential decreases in the conductance and transconductance with increase of defects in the MLG were observed, which could be explained by the percolation and the variable range hopping conduction. An enhancement of p-type nature with increasing disorders was considered to be the result of oxygen doping in the graphene sheets introduced by oxygen plasma.