Growth and nanomechanical characterization of nanoscale 3D architectures grown via focused electron beam induced deposition.

Nanomechanical measurements of platinum-carbon 3D nanoscale architectures grown via focused electron beam induced deposition (FEBID) were performed using a nanoindentation system in a scanning electron microscope (SEM) for simultaneous in situ imaging. Compression tests were used to estimate the modulus of the platinum-carbon deposits to be in the range of 8.6-10.

Biocompatibility evaluation of porous ceria foams for orthopedic tissue engineering.

Ceria ceramics have the unique ability to protect cells from free radical-induced damage, making them materials of interest for biomedical applications. To expand upon the understanding of the potential of ceria as a biomaterial, porous ceria, fabricated via direct foaming, was investigated to assess its biocompatibility and its ability to scavenge free radicals. A mouse osteoblast (7F2) cell line was cultured with the ceria foams to determine the extent of the foams' toxicity.

Biocompatible evaluation of barium titanate foamed ceramic structures for orthopedic applications.

The potential of barium titanate (BT) to be electrically active makes it a material of interest in regenerative medicine. To enhance the understanding of this material for orthopedic applications, the in vitro biocompatibility of porous BT fabricated using a direct foaming technique was investigated. Characterization of the resultant foams yielded an overall porosity between 50 and 70% with average pore size in excess of 30 µm in diameter.