1.9 µm waveguide laser fabricated by ultrafast laser inscription in Tm:LuO ceramic.

The ultrafast laser inscription technique has been used to fabricate channel waveguides in Tm-doped LuO ceramic gain medium for the first time to our knowledge. Laser operation has been demonstrated using a monolithic microchip cavity with a continuous-wave Ti:sapphire pump source at 796 nm. The maximum output power achieved from the Tm:LuO waveguide laser was 81 mW at 1942 nm.

Nonlinear optical properties of multilayer graphene in the infrared.

A negative value for the nonlinear refraction in graphene is experimentally observed and unambiguously verified by performing a theoretical analysis arising from the conductivity of the graphene monolayer. The nonlinear optical properties of multi-layer graphene are experimentally studied by employing the Z-scan technique. The measurements are carried out at 1150, 1550, 1900 and 2400 nm with a 100-femtosecond laser source.

Correlating structure with non-linear optical properties in xAs40Se60·(1-x)As40S60 glasses.

A series of xAs40Se60·(100 - x)As40S60 glasses, where x = 0, 25, 33, 50, 67, 75 and 100 mol% As40Se60, has been studied using neutron and X-ray total scattering, Raman spectroscopy and (77)Se MAS-NMR. The results are presented with measurements of non-linear refractive indices, n2, and densities. There is no evidence for the formation of homopolar bonds in these glasses, but neutron correlation functions suggest that there is a non-random distribution of sulfur and selenium atoms in sulfur-rich glasses.

Broadband infrared supercontinuum generation in hexagonal-lattice tellurite photonic crystal fiber with dispersion optimized for pumping near 1560 nm: reply.

We respond to the comment submitted by Xian Feng on our recent Letter, Opt. Lett.38, 4679 (2013).

Two Octaves Supercontinuum Generation in Lead-Bismuth Glass Based Photonic Crystal Fiber.

In this paper we report a two octave spanning supercontinuum generation in a bandwidth of 700-3000 nm in a single-mode photonic crystal fiber made of lead-bismuth-gallate glass. To our knowledge this is the broadest supercontinuum reported in heavy metal oxide glass based fibers. The fiber was fabricated using an in-house synthesized glass with optimized nonlinear, rheological and transmission properties in the range of 500-4800 nm.

Broadband infrared supercontinuum generation in hexagonal-lattice tellurite photonic crystal fiber with dispersion optimized for pumping near 1560 nm.

We report on supercontinuum generation (SG) in a hexagonal lattice tellurite photonic crystal fiber (PCF). The fiber has a regular lattice with a lattice constant Λ = 2 μm, linear filling factor d/Λ = 0.75, and a solid core 2.

Two dimensional interferometric optical trapping of multiple particles and Escherichia coli bacterial cells using a lensed multicore fiber.

Two dimensional interferometric trapping of multiple microspheres and Escherichia coli has been demonstrated using a multicore fiber lensed with an electric arc fusion splicer. Light was coupled evenly into all four cores using a diffractive optical element. The visibility of the fringes and also the appearance of the lattice can be altered by rotating a half wave-plate.

Dual-beam interference from a lensed multicore fiber and its application to optical trapping.

A multicore all-fiber probe is demonstrated that has been fabricated using an electric arc fusion splicer. Interference of the fiber output when coherent light is coupled into two cores is investigated. The properties of the fringes created when the fiber is probing different media were found to be in general agreement with a beam propagation method simulation.

Ultrafast laser inscription of Bragg-grating waveguides using the multiscan technique.

We report the fabrication of high-strength (>30 dB) first order Bragg-grating waveguides in borosilicate glass substrates using ultrafast laser inscription. The cross section of each waveguide was controlled using the well known multiscan fabrication technique, where the desired waveguide cross section is constructed by scanning the sample through the laser focus multiple times. In order to fabricate high-strength gratings, it was therefore necessary to precisely control and spatially synchronize the refractive index modulations imprinted in the material by each scan.

Mid-infrared spectral broadening in an ultrafast laser inscribed gallium lanthanum sulphide waveguide.

We report the successful fabrication of mid-infrared waveguides written in a gallium lanthanum sulphide (GLS) substrate via the ultrafast laser inscription technique. Single mode guiding at 2485 nm and 3850 nm is observed. Spectral broadening spanning 1500 nm (-15dB points) is demonstrated under 3850 nm excitation.

Ultrafast laser inscription of near-infrared waveguides in polycrystalline ZnSe.

We report the successful fabrication of a low-loss near-IR waveguide in polycrystalline ZnSe using ultrafast laser inscription. The waveguide, which was inscribed using the multiscan fabrication technique, supported a well-confined mode at 1.55 μm.

Generation of supercontinuum and its theoretical study in three-ring silica microstructured optical fibers.

We report supercontinuum generation in nonlinear microstructured optical fibers (MOFs) especially fabricated in a two-step stack and draw process having three rings of airholes. High air-filling fraction (>0.9) is obtained in a simple and straightforward way during the drawing process which is essential to enhance nonlinearity.

Experimental demonstration of spectral broadening in an all-silica Bragg fiber.

We present the first report on experimental observation of nonlinear spectral broadening in an all-solid photonic band gap Bragg fiber of relatively large mode area approximately 62 microm(2). The theoretically designed Bragg fiber for this specific application was fabricated by the well known MCVD technique. Nonlinear spectral broadening was observed by launching high power femtosecond pulses of 1067 nm pump wavelength.

Fiber Bragg gratings inscribed using 800nm femtosecond laser and a phase mask in single- and multi-core mid-IR glass fibers.

For the first time, Fiber Bragg grating (FBG) structures have been inscribed in single-core passive germanate and three-core passive and active tellurite glass fibers using 800 nm femtosecond (fs) laser and phase mask technique. With fs peak power intensity in the order of 10(11)W/cm(2), the FBG spectra with 2nd and 3rd order resonances at 1540 and 1033 nm in the germanate glass fiber and 2nd order resonances at approximately 1694 and approximately 1677 nm with strengths up to 14 dB in all three cores in the tellurite fiber were observed. Thermal responsivities of the FBGs made in these mid-IR glass fibers were characterized, showing average temperature responsivity approximately 20 pm/ degrees C.

Multiple rare earth emissions in a multicore tellurite fiber with a single pump wavelength.

A three-core tellurite glass fiber having different combinations of rare earth oxide dopants in each core has been fabricated using shaped die-extrusion. Three cores, doped with Ho(3+)-Tm(3+)-Yb(3+), Er(3+)-Ce(3+), and Tm(3+)-Yb(3+) respectively, exhibited visible upconversion (blue, green and red) and infrared emissions at 1.4 microm, 1.

Supercontinuum generation in an ultrafast laser inscribed chalcogenide glass waveguide.

The authors report supercontinuum generation in an ultrafast laser inscribed chalcogenide glass waveguide. The waveguides were fabricated using a Yb:glass cavity-dumped femtosecond oscillator with 600- kHz repetition rate. The waveguides were pumped using an optical parametric amplifier tuned to 1500 nm with a bandwidth of 100 nm.

Spectral narrowing in coherent rayleigh scattering.

Spectral narrowing of the coherent Rayleigh scattering line shape in a room temperature CO(2) gas (2.5 x 10(23) m(-3)) with intense fields in the 10(15) W m(-2) range is observed. The line shape saturates to a width of approximately half that observed at low pump intensities and indicates a transition from scattering primarily from untrapped molecules to that from both trapped and untrapped molecules that are localized by the deep (60 K) optical potentials produced by the pump beams.

Ultrafast-laser inscription of a three dimensional fan-out device for multicore fiber coupling applications.

A fan-out device has been fabricated using ultrafast-laser waveguide-inscription that enables each core of a multicore optical fiber (MCF) to be addressed by a single mode fiber held in a fiber V-groove array (FVA). By utilizing the unique three-dimensional fabrication capability of this technique we demonstrate coupling between an FVA consisting of a one-dimensional array of fibers and an MCF consisting of a two-dimensional array of cores. When coupled to all cores of the MCF simultaneously, the average insertion loss per core was 5.

Thermal sensitivity of tellurite and germanate optical fibers.

The temperature coefficients of optical phase have been measured at 1536 nm wavelength for short fiber Fabry-Perot cavities of tellurite and germanate glass fibers spliced to silica fiber. The results are consistent with the thermal expansion and thermo-optic coefficients of the bulk glasses.

Femtosecond laser inscription of optical waveguides in Bismuth ion doped glass.

We report on the fabrication of high quality embedded channel waveguides inside Bi-doped silicate glass using femtosecond waveguide inscription. Waveguides are fabricated using both single and multi-scan fabrication techniques. Refractive index modifications of up to Deltan = 4.

Narrow-band coherent Rayleigh scattering in a flame.

We report on the application of coherent Rayleigh scattering (CRS) to the measurement of temperature in a flame using narrow bandwidth pump and probe fields. High resolution measurements of the line shape were used to derive flame temperature based on fits to the line shape. An uncertainty in the temperature of 3% was determined utilizing a CRS model that includes scattering from a multicomponent gas for the first time.