Fabrication of Robust Superhydrophobic Polyester Fabrics with Photothermal Conversion and Oil-Water Separation Performance through Deposition of Natural Polyphenols.

Superhydrophobic polyester (PET) fabrics were created by increasing fabric surface roughness and decreasing surface energy through interactions between natural polyphenols, ferrous sulfate heptahydrate, and hexadecyltrimethoxysilane. The superhydrophobic fabric can be obtained with different natural polyphenols, including tannic acid, ferulic acid, gallic acid, guaiacol, and caffeic acid. Durability tests were carried out on the superhydrophobic PET fabric, investigating resistance to washing, rubbing, UV aging, acids, alkalis, and organic reagents.

Facile fabrication of superhydrophobic polyester fabric based on rapid oxidation polymerization of dopamine for oil-water separation.

Through the special chemical structure of dopamine (DA), superhydrophobic polyester (PET) fabric was fabricated by introducing the low surface energy substance hexadecyltrimethoxysilane (HDS) into the PET fabric and chelating Fe ions with phenolic hydroxyl groups of polydopamine (PDA) to form a rough surface. The water contact angle (WCA) of the prepared PDA/Fe/HDS PET fabric was higher than 160° and the scrolling angle (SA) was lower than 2.09°.