Achieving Ultralow Wear with Stable Nanocrystalline Metals.

Recent work suggests that thermally stable nanocrystallinity in metals is achievable in several binary alloys by modifying grain boundary energies via solute segregation. The remarkable thermal stability of these alloys has been demonstrated in recent reports, with many alloys exhibiting negligible grain growth during prolonged exposure to near-melting temperatures. Pt-Au, a proposed stable alloy consisting of two noble metals, is shown to exhibit extraordinary resistance to wear.

Evaluating Deformation-Induced Grain Orientation Change in a Polycrystal During In Situ Tensile Deformation using EBSD.

Using an in situ load frame within a scanning electron microscope, a microstructural section on the surface of an annealed tantalum (Ta) polycrystalline specimen was mapped at successive tensile strain intervals, up to ~20% strain, using electron backscatter diffraction. A grain identification and correlation technique was developed for characterizing the evolving microstructure during loading. Presenting the correlated results builds on the reference orientation deviation (ROD) map concept where individual orientation measurements within a grain are compared with a reference orientation associated with that grain.