Effect of sulfur on synergistic corrosion behavior of Q235 and 16Mn steel in sodium aluminate solution.

In this study, the corrosion electrochemistry and corrosion behavior of two steels were studied under the simulated alumina production conditions. The corrosion rate of 16Mn steel is greater than that of Q235 steel. The effect of S concentration on corrosion rate was significantly higher than that of SO.

Effect of Corrosion Temperature on the Corrosion of Q235 Steel and 16Mn Steel in Sodium Aluminate Solutions.

This study investigates the effect of corrosion temperature on the corrosion of Q235 steel and 16Mn steel in the sodium aluminate solution using the weight loss method and electrochemical method. The results indicate that the corrosion rates of two steels show an increasing trend with the temperature and that of Q235 steel increases more than that of 16Mn steel at higher temperatures. The corrosion products have changed from four forms at 25 °C to two forms at 65 and 110 °C, namely, the octahedral particles and the bulk particles formed by the flocculent aggregation.