On the Change in Hydrogen Diffusion and Trapping Behaviour of Pearlitic Rail Steel at Different Stages of Production.

To avoid hydrogen flaking in rail production, it is of crucial importance to understand the differences in hydrogen diffusion and trapping between different production steps. Therefore, as-cast unfinished material was compared with two finished rails, hot-rolled and head-hardened, using electron backscattered diffraction (EBSD), electrochemical permeation, and thermal desorption spectroscopy (TDS). A significant increase in dislocation density was in the head-hardened rail compared with the other material states.