Analyzing the Effects of Heat Treatment on SMAW Duplex Stainless Steel Weld Overlays.

Duplex stainless steel (DSS) has a reasonably high resistance to chloride stress corrosion cracking for offshore and marine applications. However, DSS weld overlay has not been successfully demonstrated due to some inherent problems in achieving pitting and crevice corrosion resistance. In this research work, isothermal heat treatments (350, 650 and 1050 °C) with and different cooling rates have been performed DMR249 Grade A by using shield metal arc welding (SMAW) with an E2209 electrode.

The Influence of Post Weld Heat Treatment Precipitation on Duplex Stainless Steels Weld Overlay towards Pitting Corrosion.

Duplex stainless steels (DSSs) are complex materials and they have been widely used in the marine environment and gas industries, primarily offering a better resistance of pitting corrosion and good mechanical properties. In the present work, the effects of heat treatment on duplex stainless steel (DSS) weld overlay samples that were heat treated at three different temperatures, namely 350 °C, 650 °C, and 1050 °C, and followed by air cooling and water quenching were studied. Stress relief temperature at 650 °C had induced sigma phase precipitation in between delta ferrite and austenite (δ/γ) grain boundaries, resulting in the loss of corrosion resistance in the weld metal.