Shear bond strength between nickel-chromium and human dentine using a dual-cure, self-adhesive universal resin luting agent.

The adhesive property of a dual-cure, self-adhesive universal resin luting agent (Rely X Unicem, 3M ESPE) between nickel-chromium (Ni-Cr) and human dentine was compared with three conventional resin luting agents (Calibra, Dentsply; Panavia-F, Kuraray; All-bond 2 C & B cement, Bisco). Ten Ni-Cr rods were bonded to human dentine with each of the four luting agents, and were subjected to shear bond test. Results showed that there was no significant difference in shear bond strengths among the luting agents.

Chemical solubility and flexural strength of zirconia-based ceramics.

Purpose: This study was undertaken to investigate the chemical solubility and flexural strengths of 3 zirconia-based dental ceramics: In-Ceram Zirconia (IZ), In-Ceram 2000 YZ CUBES (YZ Zirconia) (Vita Zahnfabrik), and Cercon (Dentsply). A pressable lithium disilicate-reinforced glass ceramic (IPS Empress 2, Ivoclar Vivadent) was used as a control.

Materials And Methods: Ten block specimens (12 x 6 x 4 mm) of each ceramic material were prepared for chemical solubility testing.

Mathematical analysis of occlusal rest design for cast removable partial dentures.

Aims: To establish the minimum dimensions for a non-precious cast metal occlusal rest by using mathematical analysis. An occlusal rest in a removable partial denture (RPD) provides vertical support and allows occlusal forces to be transmitted through the long axis of the abutment tooth.

Methods: The stress status of an occlusal rest in a posterior tooth-bounded RPD resembles that of a cantilever beam under a uniformly distributed load.

Fracture resistance of roots with thin walls restored using an intermediate resin composite layer placed between the dentine and a cast metal post.

Thin-walled roots restored using conventional cast metal post-cores are at risk of fracture. Placing a thick intermediate layer of resin-based composite (RBC), sandwiched between the root dentine and a small-diameter metal post or dowel, may improve the fracture resistance of such roots. In this initial laboratory study, two similar groups each of six decoronated maxillary central incisor teeth were prepared with approximately 1.