Drying of electrically conductive hybrid polymer-gold nanorods studied with in situ microbeam GISAXS.

Gold nanorods (AuNRs) with conductive polymer shells are interesting colloidal building blocks for electronics. Hybrid particles with AuNR cores and poly(3,4-ethylenedioxythiophene) or polystyrene sulfonate (PEDOT:PSS) shells were prepared as stable aqueous dispersions. Film formation during the drying of such dispersions is known to affect the electric conductivity of the material.

Spinning Hierarchical Gold Nanowire Microfibers by Shear Alignment and Intermolecular Self-Assembly.

Hierarchical structures lend strength to natural fibers made of soft nanoscale building blocks. Intermolecular interactions connect the components at different levels of hierarchy, distribute stresses, and guarantee structural integrity under load. Here, we show that synthetic ultrathin gold nanowires with interacting ligand shells can be spun into biomimetic, free-standing microfibers.

Templated Self-Assembly of Ultrathin Gold Nanowires by Nanoimprinting for Transparent Flexible Electronics.

We fabricated flexible, transparent, and conductive metal grids as transparent conductive materials (TCM) with adjustable properties by direct nanoimprinting of self-assembling colloidal metal nanowires. Ultrathin gold nanowires (diameter below 2 nm) with high mechanical flexibility were confined in a stamp and readily adapted to its features. During drying, the wires self-assembled into dense bundles that percolated throughout the stamp.

Sintering of ultrathin gold nanowires for transparent electronics.

Ultrathin gold nanowires (AuNWs) with diameters below 2 nm and high aspect ratios are considered to be a promising base material for transparent electrodes. To achieve the conductivity expected for this system, oleylamine must be removed. Herein we present the first study on the conductivity, optical transmission, stability, and structure of AuNW networks before and after sintering with different techniques.