Hybrid naphthalenediimide/zinc phosphonate materials (NDI/Zn) were prepared by mixing solutions of ,'-bis(2-phosphonoethyl)-1,4,5,8-naphthalenediimide (PNDI) and zinc nitrate, resulting in the precipitation of the desired compounds. Samples precipitated from water and ,-dimethylformamide (DMF) were produced. The obtained samples had the expected elemental composition, and the presence of naphthalenediimides (NDI) was ascertained by infrared and UV-visible spectroscopy.

Layer-by-Layer Naphthalenediimide/Zn Phosphonate Hybrid Films Grown from Aqueous Solutions by a Simple Deposition Technique.

Hybrid thin films containing ,'-bis(2-phosphonoethyl)-1,4,5,8-naphthalenediimide (PNDI) and zinc cations (PNDI/Zn films) were built on silicon and indium tin oxide (ITO) substrates by a simple layer-by-layer deposition process. Silicon substrates primed with a layer of phosphonate groups were immersed alternately into zinc nitrate and PNDI aqueous solutions, yielding PNDI/Zn films containing up to 40 layers. ITO substrates, on the other hand, were used without priming, and the deposition sequence began with a PNDI layer.