Crack Propagation in As-Extruded and Heat-Treated Mg-Dy-Nd-Zn-Zr Alloy Explained by the Effect of LPSO Structures and Their Micro- and Nanohardness.

The investigation of the crack propagation in as-extruded and heat-treated Mg-Dy-Nd-Zn-Zr alloy with a focus on the interaction of long-period stacking-ordered (LPSO) structures is the aim of this study. Solution heat treatment on a hot extruded Mg-Dy-Nd-Zn-Zr (RESOLOY) was done to change the initial fine-grained microstructure, consisting of grain boundary blocky LPSO and lamellar LPSO structures within the matrix, into coarser grains of less lamellar and blocky LPSO phases. C-ring compression tests in Ringer solution were used to cause a fracture.

Discovery of a superhard iron tetraboride superconductor.

Single crystals of novel orthorhombic (space group Pnnm) iron tetraboride FeB4 were synthesized at pressures above 8 GPa and high temperatures. Magnetic susceptibility and heat capacity measurements demonstrate bulk superconductivity below 2.9 K.

Investigation of nanoscratch processes in semiconductor materials for application to maskless patterning.

Features of nanoscratching processes with a diamond 90 degrees cube corner tip in semiconductor materials have been studied with different tip orientations and scratch procedures: constant and linearly increasing normal load during scratching, multi-scratching and the direct analysis of the generated scratch by re-scanning the scratch with a strongly reduced normal load. These scratch functions allowed a detailed investigation of the materials response due to the mechanical deformation process. Elastic material recovery, plastic deformation and material removal contribute to the generation of scratch groove profiles.