Evaluation of the corrosion resistance of a Ni-P coating deposited on additive manufacturing steel: A dataset.

This article presents the data set obtained for the research work entitled "Effect of a Ni-P coating on the corrosion resistance of an additive manufacturing carbon steel immersed in a 0.1 M NaCl solution" [1]. Microstructural, mechanical, and electrochemical characterization (using the electrochemical impedance and electrochemical noise spectroscopy technique) is performed on a material obtained by additive manufacturing and the influence of a Ni-P coating on it.

Enhancement in Curie Temperature of Yttrium Iron Garnet by Doping with Neodymium.

The effect of the substitution of Y by Nd on the structural and magnetic properties of neodymium-doped yttrium iron garnet, NdYFe₅O with in the range of 0⁻2.5, is presented. Oxide powders of Fe₂O₃, Nd₂O₃, and Y₂O₃ were mixed in a stoichiometric ratio and milled for 5 h using high-energy ball milling, before being uniaxially pressed at 900 MPa and annealed at 1373 K for 2 h to obtain NdYFe₅O (0 ≤ ≤ 2.