Enhanced Fatigue Limit in Ultrafine-Grained Ferritic-Martensitic Steel.

The influence of the ultrafine-grained (UFG) structure on the fatigue endurance limit and the nature of fatigue failure have been studied. It is shown that the formation of the UFG structure containing carbides and the coincidence site lattice relationship (CSL) and twin boundaries leads to an increase in the fatigue endurance limit. To study the mechanisms of fatigue failure, scanning and transmission electron microscopy and X-ray diffraction analysis were used.