Effect of Natural Inhibitors on the Corrosion Properties of Grade 2 Titanium Alloy.

This study investigates the effects of natural inhibitors (pomegranate, algae, and tomato extracts) on the corrosion resistance of titanium (grade 2). To deepen understanding the inhibition mechanism, Molecular Dynamic (MD) and Monte Carlo (MC) simulations were employed to analyze adsorption behaviors and identify optimal adsorption sites on titanium oxide (TiO) surfaces for compounds within the inhibitors. Results indicate non-flat adsorption orientations, with pomegranate peel extract components showing superior inhibition capabilities, attributed to the formation of strong O-H chemical bonds with the TiO surface.

Correlation of Lack of Fusion Pores with Stress Corrosion Cracking Susceptibility of L-PBF 316L: Effect of Surface Residual Stresses.

Stress corrosion cracking (SCC) of laser powder bed fusion-fabricated 316L was studied under the variation in energy input density to emulate the existence of distinctive types of defects. Various electrochemical polarization measurements were performed in as-received polished and ground states, to elucidate the effect of defect type on corrosion and SCC behaviour in marine solution. The results revealed severe localized corrosion attack and SCC initiation for specimens with a lack of fusion pores (LOF).