Solid Electrolyte Interphase Layer Formation during Lithiation of Single-Crystal Silicon Electrodes with a Protective Aluminum Oxide Coating.

The lithiation of crystalline silicon was studied over several cycles using operando neutron reflectometry over six cycles. A thin layer of aluminum oxide was employed as an artificial coating on the silicon to suppress the solid electrolyte interphase (SEI) layer-related aging effects. Initially, the artificial SEI prevented side effects but led to increased lithium trapping.