Efficient Production of Segmented Carbon Nanofibers via Catalytic Decomposition of Trichloroethylene over Ni-W Catalyst.

The catalytic utilization of chlorine-organic wastes remains of extreme importance from an ecological point of view. Depending on the molecular structure of the chlorine-substituted hydrocarbon (presence of unsaturated bonds, intermolecular chlorine-to-hydrogen ratio), the features of its catalytic decomposition can be significantly different. Often, 1,2-dichloroethane is used as a model substrate.

Comparative Study on Carbon Erosion of Nickel Alloys in the Presence of Organic Compounds under Various Reaction Conditions.

The processes of carbon erosion of nickel alloys during the catalytic pyrolysis of organic compounds with the formation of carbon nanofibers in a flow-through reactor as well as under reaction conditions in a close volume (Reactions under Autogenic Pressure at Elevated Temperature, RAPET) were studied. The efficiency of the ferromagnetic resonance method to monitor the appearance of catalytically active nickel particles in these processes has been shown. As found, the interaction of bulk Ni-Cr alloy with the reaction medium containing halogenated hydrocarbons (1,2-dichloroethane, 1-iodobutane, 1-bromobutane) results in the appearance of ferromagnetic particles of similar dimensions (~200-300 nm).

Synthesis of Chlorine- and Nitrogen-Containing Carbon Nanofibers for Water Purification from Chloroaromatic Compounds.

Chlorine- and nitrogen-containing carbon nanofibers (CNFs) were obtained by combined catalytic pyrolysis of trichloroethylene (CHCl) and acetonitrile (CHCN). Their efficiency in the adsorption of 1,2-dichlorobenzene (1,2-) from water has been studied. The synthesis of CNFs was carried out over self-dispersing nickel catalyst at 600 °C.