Radiation Effects in Tungsten and Tungsten-Copper Alloys Treated with Compression Plasma Flows and Irradiated with He Ions.

The paper presents the results of studying the structure and phase state of tungsten and tungsten-copper alloy after pulsed action of compression plasma flows and irradiation with helium ions. The compression plasma flows were used to modify the surface layer of tungsten, as well as to create an alloy based on tungsten and copper. Using scanning electron microscopy and X-ray structural analysis, the formation of radiation defects on the tungsten surface was detected in the form of local areas of exfoliation and destruction, which begin to form at helium ion irradiation doses of 2 × 10 cm.

Structure and Phase Composition of WNb Alloy Formed by the Impact of Compression Plasma Flows.

The results of a tungsten-niobium alloy synthesis by the impact of pulsed compression plasma flows are presented. Tungsten plates with a 2 μm thin niobium coating were treated with dense compression plasma flows generated by a quasi-stationary plasma accelerator. The plasma flow with an absorbed energy density of 35-70 J/cm and pulse duration of 100 μs melted the niobium coating and a part of the tungsten substrate, which caused liquid-phase mixing and WNb alloy synthesis.