High-Temperature Salt Flux Crystal Growth of New Lanthanide Molybdenum Oxides, Ln5Mo2O12 Ln = Eu, Tb, Dy, Ho, and Er: Magnetic Coupling within Mixed Valent Mo(IV/V) Rutile-Like Chains.

Five new lanthanide molybdenum oxides containing mixed valent Mo(IV/V) rutile-like chains, Ln5Mo2O12 Ln = Eu, Tb, Dy, Ho, and Er, were prepared utilizing a high-temperature molten salt flux synthesis involving an in situ reduction utilizing metallic reducing agents. All five compounds were structurally characterized by single-crystal and powder X-ray diffraction methods and were found to crystallize in the monoclinic space group C2/m. The molybdates all contain rare infinite chains consisting of MoO2O4/2 edge-sharing octahedra.

Crystal growth of four oxovanadium(IV) tartrates prepared via a mild two-step hydrothermal method: observation of spin-dimer behavior and second harmonic generation.

Four new oxovanadium(IV) tartrates, namely, A2[(VO)2(C4H4O6)(C4H2O6)(H2O)2]·(H2O)2, where A = Cs, 1, Rb, 2; K2[(VO)2(C4H2O6)2(H2O)2]·(H2O)2, 3; and Na2[(VO)2(C4H4O6)(C4H2O6)(H2O)7]·(H2O)2, 4, were prepared utilizing a two-step, mild hydrothermal route involving l-(+)-tartaric acid as the reducing agent. All four compounds were structurally characterized by single-crystal and powder X-ray diffraction methods and were found to crystallize in the non-centrosymmetric orthorhombic space groups P212121 for 1, 2, and 4 and C2221 for 3. The temperature dependence of the magnetic susceptibility of these compounds was measured, and 1, 2, and 4 were found to be paramagnetic down to 2 K, while 3 was found to exhibit spin-dimer behavior.