Combining Low-Emissivity Thin Coating and 3D-Printed Original Designs for Superior Fire-Protective Performance.

Three-dimensional (3D) printing is a very flexible process to design various objects of original shapes. Previous works highlighted the preparation of new multimaterials composed of an original sandwich structure made of the ethylene vinyl acetate copolymer containing 30 wt % of aluminum trihydroxide in which a hydrogel phase made of agar and vermiculite was incorporated. This original material revealed an extremely low heat release rate (HRR) (with a reduction of 86 and 64% with regard to the peak of the HRR and total heat release, respectively, when compared to the same sample without hydrogel filling) during its heat exposure at 50 kW/m according to the mass loss cone calorimetry test.

Extreme Heat Shielding of Clay/Chitosan Nanobrick Wall on Flexible Foam.

Flexible polyurethane foam (PUF) is widely used in bedding, transportation, and furniture, despite being highly flammable. In an effort to decrease the flammability of the polymer, an environmentally friendly flame retardant coating was deposited on polyurethane foam (PUF) via layer-by-layer assembly. Treated foam was subjected to three different fire scenarios, 10 s torch test, cone calorimetry, and a 900 s burn-through test, to evaluate the thermal shielding behavior of an eight bilayer chitosan/vermiculite clay nanocoating.