The influence of finishing line and luting material selection on the seating accuracy of CAD/CAM indirect composite restorations.

Objectives: This study aimed to assess the seating accuracy of resin composite CAD/CAM overlay restorations, employing various preparation designs and luting materials (pre-heated composite (HC) or resin cement (RC)).

Methods: A human molar's STL file was utilized to create 100 3D-printed resin tooth replicas, randomly distributed into 5 groups (n = 20) based on finishing line preparation designs: 1) Rounded shoulder above the dental equator - DE (SA); 2) Chamfer above the DE (CA); 3) Butt joint above the DE (BJ); 4) Rounded shoulder below the DE (SB); 5) Chamfer below the DE (CB). Digital impressions were acquired for all replicas, and restorations milled using Tetric CAD (Ivoclar Vivadent).

Stresses in Premolars Restored Using Different Post-and-Core and Crown Materials: An FEA Study.

Purpose: The aim of the present study was to investigate the influence of three post-and-core systems and two crown materials on stresses in restored premolars using Finite Element Analysis (FEA).

Materials And Methods: A maxillary second premolar 3D model was created in SolidWorks 2014 (Dassault Systémés). Severe loss of tooth structure was simulated with six restorative options: 1) glass-fiber-reinforced composite post and composite core (GFRC)+CAD/CAM leucite-reinforced glass-ceramic crown (LRC); 2) carbon-fiberreinforced composite post and composite core (CFRC)+LRC; 3) metal cast post-and-core (MPC)+LRC 4) GFRC+CAD/CAM composite resin crown (CC); 5) CFRC+CC; 6) MPC+CC.

Comparisons of ammonia- and water-based silver-containing solutions on dentin bonding and enzymatic activity: 1-yr evaluation.

Objective: To evaluate the effects of an ammonia-based and a water-based silver-containing solutions on bonding performance and matrix-metalloproteinases (MMPs) activity of a universal adhesive to dentin after 1 year of artificial aging.

Methods: Mid-coronal dentin surfaces of 60 sound human molars were exposed and the following groups were formed according to the surface pre-treatment and etching mode of the universal adhesive (Zipbond Universal, SDI) (n = 10): G1) Zipbond in the self-etch mode (ZSE); G2) Riva Star (SDI) applied before ZSE; G3) Riva Star Aqua (SDI) applied before ZSE; G4) Zipbond in the etch-and-rinse mode (ZER); G5) Riva Star applied before ZER; G6) Riva Star Aqua applied before ZER. The specimens were sectioned and subjected to microtensile bond strength (µTBS) test at baseline (T) and after 12 months (T) of artificial storage.