Templated synthesis of electroactive periodic mesoporous organosilica bridged with oligoaniline.

The synthesis and characterization of novel electroactive periodic mesoporous organosilica (PMO) are reported. The silsesquioxane precursor, N,N'-bis(4'-(3-triethoxysilylpropylureido)phenyl)-1,4-quinonene-diimine (TSUPQD), was prepared from the emeraldine base of amino-capped aniline trimer (EBAT) using a one-step coupling reaction and was used as an organic silicon source in the co-condensation with tetraethyl orthosilicate (TEOS) in proper ratios. By means of a hydrothermal sol-gel approach with the cationic surfactant cetyltrimethyl-ammonium bromide (CTAB) as the structure-directing template and acetone as the co-solvent for the dissolution of TSUPQD, a series of novel MCM-41 type siliceous materials (TSU-PMOs) were successfully prepared under mild alkaline conditions.

Electroactive oligoaniline-containing self-assembled monolayers for tissue engineering applications.

A novel electroactive silsesquioxane precursor, N-(4-aminophenyl)-N'-(4'-(3-triethoxysilyl-propyl-ureido) phenyl-1,4-quinonenediimine) (ATQD), was successfully synthesized from the emeraldine form of amino-capped aniline trimers via a one-step coupling reaction and subsequent purification by column chromatography. The physicochemical properties of ATQD were characterized using mass spectrometry as well as by nuclear magnetic resonance and UV-vis spectroscopy. Analysis by cyclic voltammetry confirmed that the intrinsic electroactivity of ATQD was maintained upon protonic acid doping, exhibiting two distinct reversible oxidative states, similar to polyaniline.