Polymerization Kinetics, Shrinkage Stress, and Bond Strength to Dentin of Conventional and Self-adhesive Resin Cements.

Purpose: To evaluate the kinetics of polymerization and shrinkage stress of resin cements, as well as their bond strength to dentin after 24-h or one-year water storage.

Materials And Methods: Three conventional resin cements were evaluated: RelyX Ultimate (RUL), Panavia V5 (PNV), and Multilink N (MLN); and three self-adhesive resin cements: RelyX Unicem 2 (RUN), Panavia SA Cement Plus (PSA), and G-CEM LinkAce (GCL). Degree of conversion (DC), maximum polymerization rate (RPmax) and gel time values were obtained using Fourier-transform infrared spectroscopy (FTIR/ATR).

Effect of dental headlights spectrum on the polymerization and working time of light-cured resin composites.

Background: The use of dental headlights is a common practice to better illuminate the operatory field and achieve excellence in restorative dentistry. However, visible light-cured dental materials can have reduced working time under headlight illumination. The aim of this study was to evaluate the influence of the spectral irradiance power of two dental headlights on the degree of polymerization and working time of light-curable dental composites.

Influence of Er:YAG laser irradiation settings on dentin-adhesive interfacial ultramorphology and dentin bond strength.

This study evaluated the effects of Erbium-doped yttrium aluminium garnet (Er:YAG) laser settings and dentin bonding agents on ultramorphological characteristics of resin-laser-irradiated dentin interfaces and dentin bond strength (BS) of these adhesive systems. Additionally, dentin depth affected by Er:YAG laser irradiations was measured. The experiments were performed on occlusal dentin surfaces of third molars that were flattened with 600-grit SiC sandpaper.

Bond Strength of Methacrylate-based Blends Containing Elastomeric Monomers and Alternative Initiators after Thermomechanical Cycling.

Purpose: To evaluate the bond strength to dentin produced by experimental adhesives formulated with an elastomeric methacrylate monomer (EMM) and an alternative initiator system based on a Thioxanthone derivative (QTX).

Materials And Methods: A self-etching primer was used. For the bonding resin, a model adhesive (G1) was formulated containing bis-GMA/TEG-DMA/HEMA (co-monomeric blend) + CQ/EDAB (initiator system).

Efficiency of polymerization of bulk-fill composite resins: a systematic review.

This systematic review assessed the literature to evaluate the efficiency of polymerization of bulk-fill composite resins at 4 mm restoration depth. PubMed, Cochrane, Scopus and Web of Science databases were searched with no restrictions on year, publication status, or article's language. Selection criteria included studies that evaluated bulk-fill composite resin when inserted in a minimum thickness of 4 mm, followed by curing according to the manufacturers' instructions; presented sound statistical data; and comparison with a control group and/or a reference measurement of quality of polymerization.

Comparing depth-dependent curing radiant exposure and time of curing of regular and flow bulk-fill composites.

The effect of restoration depth on the curing time of a conventional and two bulk-fill composite resins by measuring microhardness and the respective radiosity of the bottom surface of the specimen was investigated. 1-, 3- and 5-mm thick washers were filled with Surefil SDR Flow-U (SDR), Tetric EvoCeram Bulk Fill-IVA (TEC) or Esthet-X HD-B1 (EHD), and cured with Bluephase® G2 for 40s. Additional 1-mm washers were filled with SDR, TEC or EHD, placed above the light sensor of MARC®, stacked with pre-cured 1-, 3- or 5-mm washer of respective material, and cured for 2.

Adhesion of multimode adhesives to enamel and dentin after one year of water storage.

Objectives: This study aimed to evaluate the ultramorphological characteristics of tooth-resin interfaces and the bond strength (BS) of multimode adhesive systems to enamel and dentin.

Methods: Multimode adhesives (Scotchbond Universal (SBU) and All-Bond Universal) were tested in both self-etch and etch-and-rinse modes and compared to control groups (Optibond FL and Clearfil SE Bond (CSB)). Adhesives were applied to human molars and composite blocks were incrementally built up.

Bond Strength of a Flowable Bulk-fill Resin Composite in Class II MOD Cavities.

Purpose: To evaluate the microtensile bond strength (μTBS) of a bulk-fill low-stress resin-based composite to dentin from gingival walls of Class II MOD cavities.

Materials And Methods: Class II MOD cavities were prepared in 44 human molars with the distal and mesial proximal boxes 4 and 6 mm deep, respectively. Eight experimental groups (n = 11) were obtained by a factorial design including 1.

Influence of cavity preparation with Er,Cr:YSGG laser and restorative materials on in situ secondary caries development.

Objective: The aim of this study was to evaluate the influence of cavity preparation and restorative materials containing fluorides in the prevention of secondary caries lesion development in situ.

Methods: A total of 120 blocks obtained from human teeth were divided into two groups and standardized cavities were prepared using diamond burs (DB) or Er,Cr:YSGG-laser [20 Hz, 4.0W, 55% water, 65% air (LA)].

Effect of partially demineralized dentin beneath the hybrid layer on dentin-adhesive interface micromechanics.

Objective: To investigate the presence of non-infiltrated, partially demineralized dentin (PDD) beneath the hybrid layer for self-etch adhesive systems, and its effect on micromechanical behavior of dentin-adhesive interfaces (DAIs). This in-vitro laboratory and computer simulation study hypothesized that the presence of non-infiltrated PDD beneath the hybrid layer does not influence the mechanical behavior of the DAI of self-etch adhesive systems.

Methods: Fifteen sound third molars were restored with composite resin using three adhesive systems: Scotchbond Multipurpose (SBMP), Clearfil SE Bond (CSEB) and Adper Promp L-Pop (APLP).

Comparison of chemical aging and water immersion time on durability of resin-dentin interface produced by an etch-and-rinse adhesive.

Aim: The aim of this study was to analyze and compare the influence of short-term NaOCl-storage and long-term water storage on the microtensile bond strength (µTBS) of etch-and-rinse adhesive system to human dentin.

Materials And Methods: Thirty-six third human molars were randomly divided into 6 groups (n = 6) according to the aging protocol: G1 (water, 24 hours); G2 (water, 6 months); G3 (water, 12 months); G4 (10% sodium hypochlorite--NaOCl, 1 hour); G5 (10% NaOCl, 3 hours) and G6 (10% NaOCl, 5 hours). A two-step etch-and-rinse adhesive (Adper Single Bond 2) was applied according to the manufacturers' instructions.

Interaction morphology and bond strength of nanofilled simplified-step adhesives to acid etched dentin.

Objective: To evaluate the effect of nanofillers incorporated into adhesives on the microtensile bond strength (μ-TBS) and interfacial micromorphology to dentin.

Methods: The occlusal enamel of 5 human molars was removed and each tooth sectioned into four quarters. The exposed dentin was treated with one of the following adhesives: Adper Single Bond (SB-unfilled), OptiBond Solo Plus (OS-barium aluminoborosilicate, 400nm Ø), Prime & Bond NT (NT-colloidal silica, 7-40 nm Ø) and Adper Single Bond 2 (SB2-colloidal silica, 5nm Ø).

Analysis of the interfacial micromorphology and bond strength of adhesive systems to Er:YAG laser-irradiated dentin.

Unlabelled: This study evaluated the effects of different parameters of dentin irradiation with erbium -doped yttrium aluminum garnet (Er:YAG) laser on bond strength to dentin and analyzed the ultramorphological characteristics of resin-laser-irradiated dentin interfaces using a transmission electron microscope (TEM). Dentin surfaces were abraded with SiC paper (600 grit) or Er:YAG laser-irradiated (120/4, 140/6, 180/4, or 200/6 mJ/Hz). Three adhesive systems were tested: Single Bond Plus (3M ESPE), Clearfil Protect Bond (Kuraray Med.

Effect of pre-heated dual-cured resin cements on the bond strength of indirect restorations to dentin.

This study evaluated the effects of resin luting agents (LA) polymerized using increased temperature on the in vitro microtensile bond strength (mTBS) of indirect restorations to dentin. The occlusal dentin surfaces of 40 human third molars were exposed and flattened. The teeth were assigned to 8 groups (n = 5) according to the LA temperature (25°C o r 50°C), curing mode (dual- or self-curing mode), and product (Excite DSC/Variolink II [VII] and XP Bond/Calibra [Cal]).

Effect of the application of a casein phosphopeptide-amorphous calcium phosphate (CPP-ACP) paste and adhesive systems on bond durability of a fissure sealant.

This study aimed to evaluate the effect of the previous application of a casein phosphopeptide-amorphous calcium phosphate paste (MI Paste, MI) and adhesive systems on the bond durability of a fissure sealant. Ninety-eight enamel blocks were obtained from proximal surfaces of erupted third molars. Specimens were divided into 14 groups (n = 7) according to the previous application of MI (with and without) and the adhesive systems used (no adhesive system; hydrophobic resin of a three-step etch-and-rinse adhesive system; etch-and-rinse single-bottle adhesive system; all-in-one adhesive system; two-step self-etching adhesive system; additional phosphoric acid conditioning and all-in-one adhesive system; additional phosphoric acid conditioning and two-step self-etching adhesive system).

Influence of filler addition, storage medium and evaluation time on biaxial flexure strength and modulus of adhesive systems.

Objective: This study evaluated the effects of filler addition, storage medium and time on biaxial flexural strength and flexural modulus of six adhesive systems.

Materials And Methods: The adhesives were either unfilled resins: Single Bond, Prime&Bond 2.1 and One-Step; or filled resins: Single Bond Plus, Prime&Bond NT and One-Step Plus.

Light-activation through indirect ceramic restorations: does the overexposure compensate for the attenuation in light intensity during resin cement polymerization?

Objectives: This study evaluated the effects of light exposure through simulated indirect ceramic restorations (SICR) on hardness (KHN) of dual-cured resin cements (RCs), immediately after light-activation and 24 h later.

Material And Methods: Three dual-cured RCs were evaluated: Eco-Link (Ivoclar Vivadent), Rely X ARC (3M ESPE), and Panavia F (Kuraray Medical Inc.).

Effects of Er:YAG laser irradiation on the microtensile bond strength to bleached enamel.

Objective: The objective of this study was to evaluate the influence of different Er:YAG laser (λ = 2.94  μm) energy parameters on the microtensile bond strength (μTBS) and superficial morphology of bovine enamel bleached with 16% carbamide peroxide.

Background: Laser irradiation could improve adhesion to bleached enamel surfaces.

Microtensile bond strength of resin composite to dentin treated with Er:YAG laser of bleached teeth.

The objective of this study was to evaluate the influence of Er:YAG laser (λ = 2.94 μm) on microtensile bond strength (μTBS) and superficial morphology of bovine dentin bleached with 16% carbamide peroxide. Forty bovine teeth blocks (7 × 3 × 3 mm(3)) were randomly assigned to four groups: G1- bleaching and Er:YAG irradiation with energy density of 25.

Effect of curing mode on the hardness of dual-cured composite resin core build-up materials.

This study evaluated the Knoop Hardness (KHN) values of two dual-cured composite resin core build-up materials and one resin cement exposed to different curing conditions. Two dual-cured core build-up composite resins (LuxaCore-Dual, DMG; and FluoroCore2, Dentsply Caulk), and one dual-cured resin cement (Rely X ARC, 3M ESPE) were used in the present study. The composite materials were placed into a cylindrical matrix (2 mm in height and 3 mm in diameter), and the specimens thus produced were either light-activated for 40 s (Optilux 501, Demetron Kerr) or were allowed to self-cure for 10 min in the dark (n = 5).

Bacterial adhesion on smooth and rough titanium surfaces after treatment with different instruments.

Background: Newly formed biofilm after implant debridement may challenge the long-term stability of peri-implant therapy. This in vitro study aimed to assess the roughness and adherence of Streptococcus sanguinis after treatment of smooth and rough titanium surfaces with an erbium-doped:yttrium, aluminum, and garnet (Er:YAG) laser, metal and plastic curets, and an air-powder abrasive system.

Methods: Forty titanium disks with smooth-machined surfaces and 40 with sand-blasted and acid-etched surfaces were divided into the following treatment groups: Er:YAG laser; plastic curet; metal curet, and air-powder abrasive system.

Effects of surface texture and etching time on roughness and bond strength to ground enamel.

Aim: The aim of this study was to assess the influence of surface texture and etching technique on surface roughness (Ra) and bond strength (BS) to enamel and to determine if a correlation exists between them.

Methods And Materials: Fifty enamel blocks were either roughened with 600-grit SiC paper or polished with diamond pastes. After establishing ten test groups (n=5), the initial Ra measurements, rough (R) and smooth (S) enamel surfaces were etched according to the following protocols: Group 1(R)/Group 2(S)- 35% phosphoric acid gel (H3PO4) for 15 seconds; Group 3(R)/Group 4(S)- 35% H3PO4 for 60 seconds; Group 5(R)/Group 6(S)- Clearfil SE Bond primer for 20 seconds; Group 7(R)/Group 8(S)- self-etching primer (SEP) for 60 seconds; Group 9(R)/Group 10(S)- 35% H3PO4 for 15 seconds + SEP for 20 seconds.

All-ceramic inlay-retained fixed partial bridge using a CAD-CAM produced Y-TZP framework and fluoroapatite veneering ceramic: a clinical report.

All-ceramic materials have become an excellent option for both anterior and posterior fixed partial dentures (FPDs) due to advances in esthetic and mechanical properties. This clinical report describes the use of an all-ceramic inlay-retained three-unit FPD for replacement of a maxillary second premolar. Prosthetic restorative materials consisted of a CAD-CAM processed presintered yttrium stabilized zirconium oxide (Y-TZP) framework and a fluoroapatite veneering ceramic.

In vitro antimicrobial activity of peroxide-based bleaching agents.

Antibacterial activity of 4 commercial bleaching agents (Day White, Colgate Platinum, Whiteness 10% and 16%) on 6 oral pathogens (Streptococcus mutans, Streptococcus sobrinus, Streptococcus sanguinis, Candida albicans, Lactobacillus casei, and Lactobacillus acidophilus) and Staphylococcus aureus were evaluated. A chlorhexidine solution was used as a positive control, while distilled water was the negative control. Bleaching agents and control materials were inserted in sterilized stainless-steel cylinders that were positioned under inoculated agar plate (n = 4).