Evaluation of bond strength and internal adaptation between the dental cavity and adhesives applied in one and two layers.

This research evaluated the influence of the number of adhesive layers of three adhesive systems on microtensile bond strength (microTBS) to dentin and the internal adaptation between the dental structure and the resin composite restoration. Two cavities (C-factor = 3) were made on the buccal surfaces of 30 bovine incisors. Scotchbond Multi-Purpose (MP), Adper Single Bond 2 (SB) and Clearfil SE Bond (CSB) were applied in one layer (MP-I, SB-I and CSB-I) and in two layers (MP-II, SB-II and CSB-II).

Optical density and chemical composition of microfilled and microhybrid composite resins.

This study evaluated the optical density of two microfilled and two microhybrid resins, as well as the composition of these materials with regard to their optical density. Cavities prepared in 12 2-mm- or 4-mm-thick acrylic plastic plates were filled with Z250 (3M-ESPE), A110 (3M-ESPE), Charisma (Heraeus-Kulzer) and DurafillVS (Heraeus-Kulzer). The resin increments (2-mm-thick) were light-cured for 40 s.

Shear bond strength of indirect resin to NiCr with different metal surface preparations.

This study sought to evaluate the shear bond strength of indirect resin to nickel chromium (NiCr) after different surface preparations. Sixty-four metal samples were divided into four groups, according to surface preparation, and two layers of opaque resin and three layers of body resin were applied. Each group was divided into two subgroups based on storage period in distilled water at 37 degrees C.