Mechanically Robust and UV-Curable Shape-Memory Polymers for Digital Light Processing Based 4D Printing.

4D printing is an emerging fabrication technology that enables 3D printed structures to change configuration over "time" in response to an environmental stimulus. Compared with other soft active materials used for 4D printing, shape-memory polymers (SMPs) have higher stiffness, and are compatible with various 3D printing technologies. Among them, ultraviolet (UV)-curable SMPs are compatible with Digital Light Processing (DLP)-based 3D printing to fabricate SMP-based structures with complex geometry and high-resolution.

Highly stretchable hydrogels for UV curing based high-resolution multimaterial 3D printing.

We report a method to prepare highly stretchable and UV curable hydrogels for high resolution DLP based 3D printing. Hydrogel solutions were prepared by mixing self-developed high-efficiency water-soluble TPO nanoparticles as the photoinitiator with an acrylamide-PEGDA (AP) based hydrogel precursor. The TPO nanoparticles make AP hydrogels UV curable, and thus compatible with the DLP based 3D printing technology for the fabrication of complex hydrogel 3D structures with high-resolution and high-fidelity (up to 7 μm).

Highly Stretchable and UV Curable Elastomers for Digital Light Processing Based 3D Printing.

Stretchable UV-curable (SUV) elastomers can be stretched by up to 1100% and are suitable for digital-light-processing (DLP)-based 3D-printing technology. DLP printing of these SUV elastomers enables the direct creation of highly deformable complex 3D hollow structures such as balloons, soft actuators, grippers, and buckyball electronical switches.

Multimaterial 4D Printing with Tailorable Shape Memory Polymers.

We present a new 4D printing approach that can create high resolution (up to a few microns), multimaterial shape memory polymer (SMP) architectures. The approach is based on high resolution projection microstereolithography (PμSL) and uses a family of photo-curable methacrylate based copolymer networks. We designed the constituents and compositions to exhibit desired thermomechanical behavior (including rubbery modulus, glass transition temperature and failure strain which is more than 300% and larger than any existing printable materials) to enable controlled shape memory behavior.