A Synthetic Methodology for Preparing Impregnated and Grafted Amine-Based Silica Composites for Carbon Capture.

Recently, there has been a significant effort towards reducing or mitigating CO2 emissions through the use of carbon capture materials for point source or direct air capture (DAC) methods. This work focuses on amine-functionalized CO2 adsorbents for DAC. These materials show promise for CO2 removal because they have low regeneration energy consumption and high adsorption capacity.

Relative effects of polymer composition and sample preparation on glass dynamics.

Modern design of common adhesives, composites and polymeric parts makes use of polymer glasses that are stiff enough to maintain their shape under a high stress while still having a ductile behavior after the yield point. Typically, material compositions are tuned with co-monomers, polymer blends, plasticizers, or other additives to arrive at a tradeoff between the elastic modulus and toughness. In contrast, strong changes to the mechanics of a glass are possible by changing only the molecular packing during vitrification or even deep in the glassy state.

Effects of Thermal Aging on Molar Mass of Ultra-High Molar Mass Polyethylene Fibers.

Ultra-high molar mass polyethylene (UHMMPE) is commonly used for ballistic-resistant body armor applications due to the superior strength of the fibers fabricated from this material combined with its low density. However, polymeric materials are susceptible to thermally induced degradation during storage and use, which can reduce the high strength of these fibers, and, thus, negatively impact their ballistic resistance. The objective of this work is to advance the field of lightweight and soft UHMMPE inserts used in various types of ballistic resistant-body armor via elucidating the mechanisms of chemical degradation and evaluating this chemical degradation, as well as the corresponding physical changes, of the UHMMPE fibers upon thermal aging.

Temperature-insensitive silicone composites as ballistic witness materials: the impact of water content on the thermophysical properties.

In this work, different formulations of a room-temperature silicone composite backing material (SCBM) composed of polydimethylsiloxane (PDMS), fumed silica and corn starch were investigated using different characterization techniques, i.e., differential scanning calorimetry, thermogravimetry analysis, X-ray diffraction (XRD) and small-angle X-ray scattering, as a function of controlled relative humidity.

Effect of Elevated Temperature and Humidity on Fibers Based on 5-amino-2-(-aminophenyl) benzimidazole (PBIA).

Soft body armor is typically comprised of materials such as aramid. Recently, copolymer fibers based on the combination of 5-amino-2-(p-aminophenyl) benzimidazole (PBIA) and PPTA were introduced to the body armor marketplace. The long-term stability of these copolymer fibers have not been the subject of much research, however they may be sensitive to hydrolysis due to elevated humidity because they are condensation polymers.

Tensile Testing of Aged Flexible Unidirectional Composite Laminates for Body Armor.

Flexible Unidirectional (UD) composite laminates are commonly being used for ballistic-resistant body armor. These laminates comprise UD layers, each constructed by laminating thin layers of high-performance fibers held in place using very low modulus binder resins, with the fibers in each layer oriented parallel to each other. As these materials are used in body armor, it is important to investigate their long-term reliability, particularly with regards to exposure to temperature and humidity as these are known causes of degradation in other commonly used body armor materials.

Linking Theory to Practice: Predicting Ballistic Performance from Mechanical Properties of Aged Body Armor.

It has long been a goal of the body armor testing community to establish an individualized, scientific-based protocol for predicting the ballistic performance end of life for fielded body armor. A major obstacle in achieving this goal is the test methods used to ascertain ballistic performance, which are destructive in nature and require large sample sizes. In this work, using both the Cunniff and Phoenix-Porwal models, we derived two separate but similar theoretical relationships between the observed degradation in mechanical properties of aged body armor and its decreased ballistic performance.

Effect of Irradiation and Detection of Long-Lived Polyenyl Radicals in Highly Crystalline Ultra-High Molar Mass Polyethylene (UHMMPE) Fibers.

To improve properties such as thermal conductivity, low temperature thermal strain, and creep resistance of ultra-high molar mass polyethylene (UHMMPE) fibers, several researchers have previously undertaken efforts to crosslink these fibers using radiation. Ionizing radiation is commonly used to crosslink bulk UHMMPE in other applications, such as artificial joints. However, UHMMPE fibers differ from bulk UHMMPE in that they have a higher crystallinity (approximately 85% to 90%) and are very highly oriented during manufacturing in which the fibers are stretched 50 to 100 times their original length.

Cutting Procedures, Tensile Testing, and Ageing of Flexible Unidirectional Composite Laminates.

Many body armor designs incorporate unidirectional (UD) laminates. UD laminates are constructed of thin (<0.05 mm) layers of high-performance yarns, where the yarns in each layer are oriented parallel to each other and held in place using binder resins and thin polymer films.

Multiscale Polymer Dynamics in Hierarchical Carbon Nanotube Grafted Glass Fiber Reinforced Composites.

Carbon nanotube (CNT) grafted glass fiber reinforced epoxy nanocomposites (GFRP) present a range of stiffnesses (MPa to GPa) and length scales (m to nm) at the fiber-matrix interface. The contribution of functionalized CNT networks to the local and bulk polymer dynamics is studied here by using a combination of torsion dynamical mechanical thermal analysis (DMTA), positron annihilation lifetime spectroscopy (PALS), and neutron scattering (NS) measurements. DMTA measurements highlight a reduction in the storage modulus (') in the rubbery region and an asymmetric broadening of the loss modulus (″) peak in the -transition region.

Disentangling High Strength Copolymer Aramid Fibers to Enable the Determination of Their Mechanical Properties.

Traditionally, soft body armor has been made from poly(p-phenylene terephthalamide) (PPTA) and ultra-high molecular weight polyethylene. However, to diversify the fiber choices in the United States body armor market, copolymer fibers based on the combination of 5-amino-2-(p-aminophenyl) benzimidazole (PBIA) and the more conventional PPTA were introduced. Little is known regarding the long-term stability of these fibers, but as condensation polymers, they are expected to have potential sensitivity to moisture and humidity.

Oxidation Reactions in Kink Banded Regions of UHMMPE Fiber-Based Laminates Used in Body Armor: A Mechanistic Study.

This work demonstrates the synergy between the thermo-mechanical and humidity induced degradation as well as the oxidation reactions in the kink-banded areas of ultra-high molar mass polyethylene (UHMMPE) fiber-based laminates used in body armor. For aged materials, the energy-dispersive X-ray spectroscopy (EDS) and Fourier transform infrared spectroscopy (FTIR) results reveal high concentrations of oxygen containing products, and the EPR results demonstrate the presence of the peroxyl radicals (RO ) in the kink-banded areas. After one year of dark ambient storage, very long-lived RO radicals were observed primarily in the samples exposed to ageing conditions of elevated temperatures, humidity, and mechanical stress.

Photofading in cotton fibers dyed using red, yellow, and blue direct dyes during examination with microspectrophotometry (MSP).

Microspectrophotometry (MSP) is a rapid, nondestructive technique for the analysis of color in textile fibers. This technique combines microscopy and ultraviolet (UV)/visible (Vis) spectroscopy, allowing for very small colored samples, like dyed textile fibers, to be analyzed directly and thereby eliminates the need for time consuming and destructive extractions. While MSP is generally accepted to be a nondestructive evaluation method, a loss of color during analysis, or photofading can occur.

Enhanced durability of carbon nanotube grafted hierarchical ceramic microfiber-reinforced epoxy composites.

As carbon nanotube (CNT) infused hybrid composites are increasingly identified as next-generation aerospace materials, it is vital to evaluate their long-term structural performance under aging environments. In this work, the durability of hierarchical, aligned CNT grafted aluminoborosilicate microfiber-epoxy composites (CNT composites) are compared against baseline aluminoborosilicate composites (baseline composites), before and after immersion in water at 25 °C (hydro) and 60 °C (hydrothermal), for extended durations (90 d and 180 d). The addition of CNTs is found to reduce water diffusivities by approximately 1.