Remineralizing pretreatment using casein phosphopeptide-amorphous calcium phosphate fluoride, self-assembling peptide, and nanohydroxyapatite gel activation via invisible infrared light on the dentin microhardness and micro shear bond strength to the composite restoration.

Aim: Different remineralizing pretreatments Casein phosphopeptide-amorphous calcium phosphate fluoride (CPP-ACPF), tricalcium phosphate fluoride (TCP-F), self-assembling peptide (SAP) P11-4 and 10 % Nanohydroxyapatite (nHA) gel activation via invisible infrared light on the dentin microhardness (MH) and micro shear bond strength (µSBS) of composite restoration.

Methods: Seventy-five human molar teeth were collected and the dentinal surface of all the samples was exposed to different demineralizing solutions. (n = 15) Group 1 (demineralized dentin), Group 2 (CPP ACP), Group 3 (TCP-F), Group 4 (SAP P11-4), Group 5 (nHA gel activation via invisible infrared light).

Analysis of recurrent esthetic dental proportion of natural maxillary anterior teeth: A systematic review.

Statement Of Problem: The recurrent esthetic dental (RED) proportion has been a benchmark for the rehabilitation of the maxillary anterior teeth of North American patients. While it has been evaluated in other populations, the global application of RED proportions in the rehabilitation of maxillary anterior teeth is unclear.

Purpose: The purpose of this systematic review was to examine the existing evidence on dental proportion to evaluate the existence of RED proportions in the esthetic smile in different geographic regions.

Influence of Concentration Levels of β-Tricalcium Phosphate on the Physical Properties of a Dental Adhesive.

Our study assessed the influence of integrating 5% and 10% tricalcium phosphate (β-TCP-Ca(PO).) nanoparticles into a dental adhesive on the adhesive's bonding. To evaluate the filler nanoparticles, scanning electron microscopy (SEM), Energy Dispersive X-Ray (EDX) spectroscopy, Fourier-transform infrared (FTIR) spectroscopy, and micro-Raman spectroscopy techniques were used.

Polymer-Based Bioactive Luting Agents for Cementation of All-Ceramic Crowns: An SEM, EDX, Microleakage, Fracture Strength, and Color Stability Study.

The aim of the study was to compare microleakage and fracture loads of all ceramic crowns luted with conventional polymer resins and polymeric bioactive cements and to assess the color stability of polymeric bioactive cements. Seventy-five extracted premolar teeth were tested for fracture loads and microleakage in all-ceramic crowns cemented with two types of polymeric bioactive cements and resin cements. In addition, the degree of color change for each cement with coffee was assessed.

Surface Properties of Polymer Resins Fabricated with Subtractive and Additive Manufacturing Techniques.

This study aimed to compare the surface roughness, hardness, and flexure strength of interim indirect resin restorations fabricated with CAD-CAM (CC), 3D printing (3D), and conventional techniques (CV). Twenty disk (3 mm × Ø10 mm) and ten bar specimens (25 × 2 × 2 mm) were fabricated for the CC, 3D, and CV groups, to be used for surface roughness, micro-hardness, and flexural strength testing using standardized protocol. Three indentations for Vickers micro-hardness (VHN) were performed on each disk and an average was identified for each specimen.

Influence of TiO and ZrO Nanoparticles on Adhesive Bond Strength and Viscosity of Dentin Polymer: A Physical and Chemical Evaluation.

The present study aimed to formulate an experimental adhesive (EA) and reinforce it with 5 wt.% titanium dioxide (TiO) or zirconium oxide (ZrO) to yield 5% TiO and 5% ZrO adhesives, respectively, and then analyze the impact of this reinforcement on various mechanical properties of the adhesives. The EA contained a blend of monomers such as bisphenol A glycol dimethacrylate (BisGMA), triethylene glycol dimethacrylate (TEGDMA), 2-hydroxyethyl methacrylate (HEMA), and ethyl 4-dimethylamino benzoate and camphorquinone.

Faculty Members' Attitude Toward Establishing a Business Center in the Dental School Clinic, King Saud University.

Aims And Objectives: The aim of this study was to evaluate the faculty members' attitude toward establishing a business center in the College of Dentistry, King Saud University, Riyadh, Saudi Arabia.

Materials And Methods: A structured questionnaire comprised three sections: demographic variables such as gender and age, questions regarding the faculty's attitude toward a dental college business center, and a comparison between a business center and private clinics. Statistical analysis was performed to compare the groups with scale response variable; independent -test, analysis of variance, and factor analysis were also conducted.

A comparative evaluation of the effect of phototherapy of fiber post on its bond strength to dental composite.

The aim of the study was to evaluate the effect of diode laser as a phototherapy on surface treatment of fiber post and its bond strength to resin core build-up material. In this in-vitro study fifty fiber post of 1 mm tip-diameter and 20 mm length were used. The posts were mounted and randomly divided into 5 groups (n = 10) according to different surface treatment methods i.