Gamma irradiation induced surface modification of (PVC/HDPE)/ZnO nanocomposite for enhancing the oil removal and conductivity using COMSOL multiphysics.

Blend nanocomposite film was prepared by loadings of irradiated ZnO in ratios of (5 wt%) inside the PVC/HDPE matrix using a hot-melt extruder technique. The physical and chemical properties of the irradiated and unirradiated ZnO samples are compared. The Vis-UV spectrum of ZnO shows an absorption peak at a wavelength of 373 nm that was slightly red-shifted to 375 nm for an irradiated sample of ZnO at a dose of 25 kGy due to the defect of crystal structure by the oxygen vacancy during gamma irradiations.

Impact of γ-irradiation and SBR content in the compatibility of aminated (PVC/LLDPE)/ZnO for improving their AC conductivity and oil removal.

In some cases, blends containing PVC and LLDPE show low compatibility. Adding styrene-butadiene rubber to the PVC/LLDPE mixtures leads to a noticeable increase in tensile strength and compatibility of the blends. Also, an improvement in tensile strength is observed after incorporating SBR compatibilizer resulting in entirely different gamma irradiation doses.