Preparation of Sr-containing carbonate apatite as a bone substitute and its properties.

Sr-containing carbonate apatite (SrCAp) specimens of varied Sr contents, ranging from 0 to 13.3 mol%, were prepared through a phosphate treatment of set gypsum-and-carbonate mixture at 100°C for 7 days. Effects of Sr content in SrCAp on microstructure, osteoblast-like cell (MC3T3-E1) attachment and proliferation, and alkaline phosphatase (ALP) activity were evaluated.

Hydrothermal calcium modification of 316L stainless steel and its apatite forming ability in simulated body fluid.

To understand the feasibility of calcium (Ca) modification of type 316L stainless steel (316L SS) surface using hydrothermal treatment, 316L SS plates were treated hydrothermally in calcium chloride (CaCl(2)) solution. X-ray photoelectron spectroscopic analysis revealed that the surface of 316L SS plate was modified with Ca after hydrothermal treatment at 200°C. And the immobilized Ca increased with CaCl(2) concentration.