Influence of Alkali Activator Type on the Hydrolytic Stability and Intumescence of Inorganic Polymers Based on Waste Glass.

The main objective of this study is the synthesis and characterization of low cost alkali-activated inorganic polymers based on waste glass (G-AAIPs) using a mixture of NaOH and Ca(OH) as alkali activators, in order to improve their hydrolytic stability. This paper also presents detailed information about the influence of composition determined by X Ray Diffraction (XRD), microstructure determined by Scanning Electronic Microscopy (SEM) and processing parameters on the main properties of G-AAIP pastes. The main factors analyzed were the glass fineness and the composition of the alkaline activators.

CO Sequestration in the Production of Portland Cement Mortars with Calcium Carbonate Additions.

The paper presents the obtention and characterization of Portland cement mortars with limestone filler and nano-calcite additions. The nano-calcite was obtained by the injection of CO in a nano-Ca(OH) suspension. The resulted nano-CaCO presents different morphologies, i.

Influence of Thermal Treatment Conditions on the Properties of Dental Silicate Cements.

In this study the sol-gel process was used to synthesize a precursor mixture for the preparation of silicate cement, also called mineral trioxide aggregate (MTA) cement. This mixture was thermally treated under two different conditions (1400 °C/2 h and 1450 °C/3 h) followed by rapid cooling in air. The resulted material (clinker) was ground for one hour in a laboratory planetary mill (v = 150 rot/min), in order to obtain the MTA cements.