Wide-band 'black silicon' with atomic layer deposited NbN.

Antireflection surfaces are often utilized in optical components to reduce undesired reflection and increase absorption. We report on black silicon (b-Si) with dramatically enhanced absorption over a broad wavelength range (250-2500 nm) achieved by applying a 10-15 nm conformal coating of NbN with atomic layer deposition (ALD). The improvement is especially pronounced in the near infrared (NIR) range of 1100-2500 nm where absorption is increased by >90%.

Lithography-free shell-substrate isolation for core-shell GaAs nanowires.

A facile and scalable lithography-free technique(5) for the rapid construction of GaAs core-shell nanowires incorporating shell isolation from the substrate is reported. The process is based on interrupting NW growth and applying a thin spin-on-glass (SOG) layer to the base of the NWs and resuming core-shell NW growth. NW growth occurred in an atmospheric pressure metalorganic vapour phase epitaxy (MOVPE) system with gold nanoparticles used as catalysts for the vapour-liquid-solid growth.

Wafer-scale self-organized InP nanopillars with controlled orientation for photovoltaic devices.

A unique wafer-scale self-organization process for generation of InP nanopillars is demonstrated, which is based on maskless ion-beam etching (IBE) of InP developed to obtain the nanopillars, where the height, shape, and orientation of the nanopillars can be varied by controlling the processing parameters. The fabricated InP nanopillars exhibit broadband suppression of the reflectance, 'black InP,' a property useful for solar cells. The realization of a conformal p-n junction for carrier collection, in the fabricated solar cells, is achieved by a metalorganic vapor phase epitaxy (MOVPE) overgrowth step on the fabricated pillars.

Exceptionally strong and robust millimeter-scale graphene-alumina composite membranes.

Graphene has attracted attention as a potential strengthening material and functional component in suspended membranes as utilized in micro and nanosystems. Development of a practical and scalable fabrication process is a necessary step to allow the exceptional material properties of graphene to be fully exploited in composite structures. Using standard and scalable microfabrication processes, we fabricated free-standing chemical vapor deposition monolayer graphene-reinforced Al2O3 composite membranes, 0.