Temperature Dependence of Light Hydrocarbons Sorption and Transport in Dense Membranes Based on Tetradecyl Substituted Silicone Rubber.

Solubility-selective polymer membranes are promising materials for C hydrocarbons removal from methane and other permanent gas streams. To this end, a dense solubility-selective membrane based on crosslinked poly(tetradecyl methyl siloxane) was synthesized. Sorption of methane, ethane, and -butane in the polymer was measured in the temperature range of 5-35 °C.

Mitigating of Thin-Film Composite PTMSP Membrane Aging by Introduction of Porous Rigid and Soft Branched Polymeric Additives.

This work was focused on the mitigation of physical aging in thin-film composite (TFC) membranes (selective layer ~1 μm) based on polymer intrinsic microporosity (PTMSP) by the introduction of both soft, branched polyethyleneimine (PEI), and rigid, porous aromatic framework PAF-11, polymer additives. Self-standing mixed-matrix membranes of thicknesses in the range of 20-30 μm were also prepared with the same polymer and fillers. Based on 450 days of monitoring, it was observed that the neat PTMSP composite membrane underwent a severe decline of its gas transport properties, and the resultant CO permeance was 14% (5.

Mixed-Gas Selectivity Based on Pure Gas Permeation Measurements: An Approximate Model.

An approximate model based on friction-coefficient formalism is developed to predict the mixed-gas permeability and selectivity of polymeric membranes. More specifically, the model is a modification of Kedem's approach to flux coupling. The crucial assumption of the developed model is the division of the inverse local permeability of the mixture component into two terms: the inverse local permeability of the corresponding pure gas and the term proportional to the friction between penetrants.