Variability in stem taper surface topography affects the degree of corrosion and fretting in total hip arthroplasty.

Degradation at the modular head-neck interface in total hip arthroplasty (THA) is predominately expressed in the form of corrosion and fretting, potentially causing peri-prosthetic failure by adverse reactions to metal debris. This retrieval study aimed to quantify variations in stem taper surface topographies and to assess the influence on the formation of corrosion and/or fretting in titanium alloy stem tapers combined with metal and ceramic heads. Four hip stem designs (Alloclassic, CLS, Bicontact and SL-Plus) were characterized using high-resolution 3D microscopy, and corrosion and fretting were rated using the Goldberg scoring scheme.